In this work, a novel chitosan Schiff base 4-(2-Hydroxyaniline)pent-3-en-2-one chitosan (2-HyA-CS) and its ZnO nanocomposite (2-HyA-CS/ZnO) were sensitized and characterized by appropriate methods; FTIR, XRD, Elemental analysis, SEM, TEM and TGA. The result of characterization methods confirms the preparation of 2-HyA-CS and 2-HyA-CS/ZnO. The SEM images reveal that chitosan, 2-HyA-CS, and 2-HyA-CS/ZnO have a varied roughness and porous surfaces. The reason for this difference was attributed to the formation of Schiff base 2-HyA-CS and the presence of ZnO nanoparticles in 2-HyA-CS/ZnO. The patterns of XRD and FTIR confirm the formation of 2-HyA-CS and 2-HyA-CS/ZnO. The degree of substitution (DS) of modified chitosan 2-HyA-CS was calculated using Elemental analysis and FTIR.ATR, it was found to be 74%. The adsorption efficiency of the produced adsorbents was compared with pure chitosan to remove of Remazol Brilliant Blue R (RBBR) from an aqueous medium and antimicrobial activity. The removal percentage of RBBR by chitosan, 2-HyA-CS, and 2-HyA-CS/ZnO are 47.12%, 91.9%, and 96.56%, respectively with the following order: 2-HyA-CS/ZnO > 2-HyA-CS > chitosan. Their antimicrobial activities were studied against two Gram negative bacteria ( E. coli and P. aeruginosa), two Gram positive bacteria ( S. aureus and B. cereus) and ( C. albicans) as a yeast strain, the inhibitory zone measurements revealed that the activity of 2-HyA-CS/ZnO is excellent and higher than 2-HyA-CS and pure chitosan. The cytotoxicity of the prepared compound 2-HyA-CS and 2-HyA-CS/ZnO along with pure chitosan was estimated against two human cancer cells MCF-7 cells and HepG-2 cells, the result indicates that 2-HyA-CS/ZnO having higher Inhibitory activity against both MCF-7 and HepG-2 cells with 53.5 ± 2.86 and 27.4 ± 1.23 µg/mL respectively and 2-HyA-CS possessing moderate Inhibitory activity against both MCF-7 and HepG-2 cancer cells with IC₅₀ = 216.5 ± 7.48 and 135.6 ± 6.49 µg/ml respectively.

Plastic manufacturing depends heavily on petroleum-derived monomers like terephthalic acid, the main component of polyethylene terephthalate (PET). However, the depletion of fossil resources and increasing environmental concerns have heightened the need for sustainable alternatives. Lignocellulosic biomass has emerged as a promising resource due to its renewable, abundant, and eco-friendly nature. Understanding its chemical composition enables conversion of this biomass into platform chemicals, such as 2,5-furandicarboxylic acid (FDCA) and lactic acid, derived from cellulose and hemicellulose. These can be polymerized into bio-based plastics such as polyethylene furanoate (PEF), polylactic acid (PLA), and polyhydroxyalkanoates (PHAs), offering greener alternatives to fossil-based plastics. PEF features rigid furan rings that enhance thermal stability, mechanical strength, and barrier properties, and reduce gas permeability compared to PET. PLA is a renewable, biodegradable plastic widely used in packaging and medical applications. This review covers the chemical composition of lignocellulosic biomass cellulose, hemicellulose, and lignin, and various pretreatment strategies, chemical, physicochemical, and physical, to overcome biomass recalcitrance and improve conversion efficiency. It also highlights recent catalytic advances in transforming cellulosic carbohydrates into bio-based plastic precursors such as FDCA and lactic acid. Lastly, this review discusses polymerization pathways for producing PEF and PLA, emphasizing their role in reducing the environmental impact of polymer manufacturing and promoting green chemistry principles.

Plastic manufacturing depends heavily on petroleum-derived monomers like terephthalic acid, the main component of polyethylene terephthalate (PET). However, the depletion of fossil resources and increasing environmental concerns have heightened the need for sustainable alternatives. Lignocellulosic biomass has emerged as a promising resource due to its renewable, abundant, and eco-friendly nature. Understanding its chemical composition enables conversion of this biomass into platform chemicals, such as 2,5-furandicarboxylic acid (FDCA) and lactic acid, derived from cellulose and hemicellu-lose. These can be polymerized into bioplastics such as polyethylene furanoate (PEF) and polylactic acid (PLA), offering greener alternatives to fossil-based plastics. PEF features rigid furan rings that enhance thermal stability, mechanical strength, and barrier proper-ties, and reduce gas permeability compared to PET. PLA is a renewable, biodegradable plastic widely used in packaging and medical applications. This review covers the chem-ical makeup of lignocellulosic biomass cellulose, hemicellulose, and lignin, and various pretreatment strategies, chemical, physicochemical, and physical, to overcome biomass recalcitrance and improve conversion efficiency. It also highlights recent catalytic ad-vances in transforming lignocellulosic carbohydrates into bioplastic precursors such as FDCA and lactic acid. Lastly, the review discusses polymerization pathways for produc-ing PEF and PLA, emphasizing their role in reducing the environmental impact of poly-mer manufacturing and promoting green chemistry principles.