We report on the experimental observation of magnetic hysteresis up to room temperature in thiol-capped Au nanoparticles with 1.4 nm size. The coercive field ranges from 860 Oe at 5 K to 250 Oe at 300 K. It is estimated that the Au atoms exhibit a magnetic moment of $\mu =0.036{\mu }_B$. However, Au nanoparticles with similar size but stabilized by means of a surfactant, i.e., weak interaction between protective molecules and Au surface atoms, are diamagnetic, as bulk Au samples are. The apparent ferromagnetism is consequently associated with $5d$ localized holes generated through Au-S bonds. These holes give rise to localized magnetic moments that are frozen in due to the combination of the high spin-orbit coupling (1.5 eV) of gold and the symmetry reduction associated with two types of bonding: Au-Au and Au-S.