MXenes are a family of two-dimensional nanomaterials. Titanium carbide MXene (Ti₃C₂T_x-MXene), reported in 2011, is the first inorganic compound reported among the MXene family. In the present work, we report on the study of the composition and various physical properties of Ti₃C₂T_x-MXene nanomaterial, as well as their temperature evolution, to consider MXenes for space applications. X-ray diffraction, thermal analysis and mass spectroscopy measurements confirmed the structure and terminating groups of the MXene surface, revealing a predominant single OH layer character. The temperature dependence of the specific heat shows a Debye-like character in the measured range of 2 K–300 K with a linear part below 10 K, characteristic of conduction electrons of metallic materials. The electron density of states (DOS) calculations for Ti₃C₂OH-MXene reveal a significant DOS value at the Fermi level, with a large slope, confirming its metallic character, which is consistent with the experimental findings. The temperature dependence of electrical resistivity of the MXene samples was tested for a wide temperature range (3 K–350 K) and shows a decrease on lowering temperature with an upturn at low temperatures, where negative magnetoresistance is observed. The magnetoresistance versus field is approximately linear and increases its magnitude with decreasing temperature. The magnetization curves are straight lines with temperature-independent positive slopes, indicating Pauli paramagnetism due to conduction electrons.

In this study, the laser metal deposition (LMD) of the Inconel 625–tungsten carbide (WC) metal matrix composite was investigated. The composite coating was deposited on Inconel 625 substrate by powder method. A powder mixture containing 10 wt% of WC (5 µm) was prepared by wet mixing with dextrin binder. Coating samples obtained by low-power LMD were pore- and crack-free. Ceramic reinforcement was distributed homogenously in the whole volume of the material. Topologically close-packed (TCP) phases were formed at grain boundaries between WC and Inconel 625 matrix as a result of partial dissolution of WC in a nickel-based alloy. Line analysis of the elements revealed very small interference of the coating in the substrate material when compared to conventional coating methods. The average Vickers hardness of the coating was about 25% higher than the hardness of pure Inconel 625 reference samples.

In this work, three-dimensional (3D) shaping of aluminum nitride (AlN) UV-curable dispersions using CeraFab 7500 device equipped with the light engine emitting 365 nm wavelength (a UV-LCM device) is presented. The purpose of this study was the shaping of AlN pieces with microchannels for the future potential use as microchannel heat exchangers. The dispersions were characterized by the means of the particle size distribution, rheological measurements, and the cure depth evaluation. In shaping via UV-LCM, we applied dispersions containing 40 vol % solid load and different types of photoinitiators and their concentrations, as well as different settings of the printing parameters. Cuboidal plates with channels and cylindrical 3D structures were fabricated, debound, and sintered. For comparing ceramics properties, reference samples were prepared via uniaxial and cold isostatic pressing, using the same powder mixture as in the dispersions, and later sintered. The thermal conductivity of the sintered specimens was calculated, based on density and thermal diffusivity measurements.

The study focuses on obtaining Inconel 625-NbC composites for high-temperature applications, e.g., jet engines, waste-to-energy combusting systems or gas engine turbines, and characterizing them in terms of their microstructure and hardness improvement. Synthesis was performed utilizing Spark Plasma Sintering (SPS) at 1150 °C under the load of 45 MPa in medium vacuum (under 10⁻³ MPa) for a total time of 60 min. Four sets of samples with different Inconel 625 to NbC weight ratios were prepared (5, 10, 20, and 30 wt.%), followed by a reference sample containing no ceramic reinforcement. Obtained materials were hot-rolled at 1150 °C with a 10% reduction step and later cut and polished to perform characterization utilizing scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS) module and microhardness testing device equipped with Vickers indenter. Hardness was improved proportionally to NbC addition achieving an increase of up to 20% of reference values. Additional heat treatment was conducted on the hot-rolled samples at 1200 °C in an argon atmosphere to further observe the interaction between reinforcement and alloy. Their microstructure revealed the coarsening of precipitates within the metal matrix and partial reinforcement dissolution, which proved to be crucial to obtaining the highest quality composites with homogenous hardness improvement.

Energy harvesting from mechanical vibration of buildings is usually realized by the use of devices, in which the main element is a prismatic beam with a rectangular cross-section. The beam has been the subject of scientific research; it is usually constructed with a carrying substrate that does not have piezoelectric characteristics and from piezoelectric material. In contrast, this investigation sought to create a beam structure with a piezoelectric composite only. The entire beam structure was made of a prototype piezoelectric particulate composite. Based on courses of voltage obtained in laboratory experiments and known geometry of the specimens, a series of finite element method (FEM) simulations was performed, aiming to estimate the piezoelectric coefficient d₃₁ value at which the mentioned voltage could be achieved. In each specimen, sedimentation caused the formation of two distinct layers: top and bottom. The experiments revealed that the presented prototype piezoelectric particulate composite converts mechanical stress to electric energy in bending mode, which is used in energy harvesting from mechanical vibration. It is self-supporting and thus a carrying substrate is not required in the harvester structure.

Alumina ceramics were joined by a transient liquid phase (TLP) bonding method at relatively lower temperatures, using mixed powders of Bi₂O₃ and ZnO with different weight ratios as interlayers between the ceramic components. Bonding was achieved at 750 °C for several of the prepared interlayer mixtures, which makes the applied approach attractive due to the relatively lower joining temperature and potentially low fabrication costs. Measurements by SEM and EDX were used to study the microstructure and chemical analysis of the obtained joints. It also allowed us to investigate the diffusion mechanism occurring in the systems, which resulted in the hypothesis that Zn²⁺/ZnO diffuses through the ceramics. XRD and Raman spectra were acquired to examine the reaction products that formed during the thermal treatment. The results showed that both ZnO and Bi₂O₃ react with each other as well as with alumina to form spinel and other products.