Over the past decade, 3D printing with concrete has been widely adopted worldwide. The primary drivers for this innovation are the reduction in manual labor and the more efficient use of natural resources. New materials that are suitable for 3D printing are developed, which are characterized by rapid setting and robust physical and mechanical properties. In this study, for the first time, ternary gypsum–cement–pozzolanic (GCP) composites were developed and evaluated for use in 3D printing. These composites are associated with durability in water as Portland cement (PC) while maintaining the rapid hardening properties of gypsum. Two types of secondary gypsum—recycled plasterboard gypsum (RG) and phosphogypsum (PG)—were used as the calcium hemihydrate component. The compressive strength test showed that 37 MPa can be achieved, which is comparable to that of traditional PC-based 3D printable mixtures. For the first time in a 3D print test, it was experimentally proved that GCP mixtures have good stability and buildability up to 35 layers. According to Life Cycle Analysis, elaborated material gives a carbon footprint reduction of up to 40%, compared to traditional PC mortar, thus supporting the sustainable use of this innovative composite.

To meet 2050 climate targets, the construction sector must reduce CO₂ emissions and transition toward circular material flows. Recycled aggregates (RA) derived from construction and demolition waste (CDW) and industrial byproducts such as oil shale ash (OSA) show potential for use in concrete, although their application remains limited by standardisation and performance limitations, particularly in structural uses. This study aims to develop and evaluate low-strength, resource-efficient concrete mixtures with full replacement of natural aggregates (NA) by CDW-derived aggregates, and partial or full replacement of cement CEM II by OSA–metakaolin (MK) binder, targeting non-structural 3D-printing applications. Mechanical performance, printability, cradle-to-gate life cycle assessment, eco-intensity index, and transport-distance sensitivity for RA were assessed to quantify the trade-offs between structural performance and global warming potential (GWP) reduction. Replacing NA with RA reduced compressive strength by ~11–13% in cement-based mixes, while the aggregate type had a negligible effect in cement-free mixtures. In contrast, full cement replacement by OSA-MK binder nearly halved compressive strength. Despite the strength reductions associated with the use of waste-derived materials, RA-based cement-free 3D-printed specimens achieved ~30 MPa in compression and ~5 MPa in flexure. Replacing CEM II with OSA-MK and NA with RA lowered GWP by up to 48%, with trade-offs in the air-emission, toxicity, water and resource categories driven by the OSA supply chain. The cement-free RA mix achieved the lowest GWP and best eco-intensity, whereas the CEM II mix with RA offered the most balanced multi-impact profile. The results show that regionally available OSA and RA can enable eco-efficient, structurally adequate 3D-printed concrete for construction applications.

Ternary gypsum–cement–pozzolan (GCP) binders represent a promising low-carbon alternative to traditional Portland cement-based systems for additive 3D printing (3DP). This study presents a systematic three-stage experimental framework for the development of printable and durable GCP mixtures: (i) optimisation of gypsum–cement–metakaolin binder proportions based on a ternary diagram for 25 formulations, (ii) comparative evaluation of different pozzolanic additives and secondary gypsum sources alongside comprehensive durability testing, and (iii) adaptation of the optimised mixtures for 3DP, focusing on rheological properties. The optimal composition was determined with 55 wt% gypsum, 22.5 wt% Portland cement, and 22.5 wt% metakaolin, achieving a 28-day wet compressive strength of 36.2 MPa and a softening coefficient of 0.85. Successful integration of secondary gypsum sources was demonstrated. The GCP 3DP mixtures were developed with water/binder ratios of 0.38–0.45 and sand/binder ratios of 0.5–1.4, with an open time of 20–40 min. The mixtures exhibit pronounced thixotropic behaviour, characterised by increasing yield stress over time and relatively stable plastic viscosity. Printability tests confirmed the stable application of 29–39 layers before structural buckling. 3DP under laboratory conditions successfully demonstrated the feasibility of producing architectural and structural elements from sustainable GCP compositions.