This study investigated the valorization of industrial lignin for producing biodegradable polybutylene succinate (PBS)–lignin copolymers. PBS was blended with varying lignin contents (0–45 wt. %) and crosslinked/grafted using dicumyl peroxide (DCP). The preparation of the copolymers by reactive extrusion was successful, with mechanical, thermal, and morphological properties comprehensively analyzed. Lignin addition decreased tensile strength but improved stiffness (modulus) and thermal stability. Crosslinking with DCP improved the interfacial adhesion between PBS and lignin, resulting in better flexural performance at moderate lignin levels. Differential scanning calorimetry showed that lignin initially improved the crystallization temperature, but hindered it at higher concentrations due to its rigid, aromatic structure. Scanning electron microscopy analysis showed poor interfacial adhesion in PBS–lignin blends, but the surface morphology improved in crosslinked PBS–lignin copolymers, with less phase separation observed. An optimal lignin concentration appeared to depend on the property of interest. While 30% lignin provided the best improvement in flexural strength, 20% lignin offered a more balanced enhancement for most properties without the severe reduction in tensile strength observed at higher lignin contents.

The generation of over 150 million tons of hemp waste annually is as much of a sustainability challenge as it is an opportunity for the circular bioeconomy. This review provides a critical analysis of the recent trends in the use of industrial hemp waste as a precursor to producing sustainable bioproducts. The objective is to synthesize the current state of knowledge and to identify the various pathways for valorizing hemp waste beyond the traditional applications. The methodology involved the systematic assessment of the recent literature to identify the applications in textiles, biocomposites, packaging, and, most importantly, advanced areas such as hemp-based carbon materials for storing energy, biomedical materials, and smart biomaterials. Findings showed that hemp waste is a versatile material for creating high-value products, as it shows promise in carbon electrodes for supercapacitors as well as reinforcement for 3D-printed biocomposites. However, there are some limitations in terms of standardization and scalability. The review concludes that future progress depends on multidisciplinary research to optimize conversion and utilization processes, including the development of comprehensive life-cycle assessments and reliable supply chains.

This study examines the effects of kraft lignin, milled hemp stalks, and dicumyl peroxide (DCP) crosslinking on polybutylene succinate (PBS) composites, focusing on rheological, mechanical, and thermal properties as well as accelerated weathering and fungal performance. Two composite series were produced via twin-screw extrusion, (a) simple blends (B-series) and (b) DCP-crosslinked formulations (R-series), with emphasis on hybrid lignin–hemp composites (B-PLH and R-PLH). Rheological analysis showed that hemp fiber increased viscosity, while lignin reduced it, and DCP further enhanced shear-thinning behavior. Mechanical testing confirmed that R-PLH exhibited a 16% increase in flexural strength (42.6 MPa) and a 2.4-fold increase in flexural modulus (1785 MPa) over neat PBS, but tensile strength declined by 19%. Thermal analysis revealed a 14–26% reduction in mass loss rate and increased char formation (up to 16.3% in R-PLH), indicating improved thermal stability. Water absorption showed that hemp fibers increased hydrophilicity, further increased by DCP. Accelerated weathering led to significant color change and surface degradation, particularly in R-PLH. Despite lignocellulosic content, all composites exhibited ≤2% fungal degradation, indicating limited mass loss due to fungal exposure under conditions used in this study. Overall, B-PLH and R-PLH offer a balance of stiffness and thermal stability, though trade-offs in tensile strength and weathering resistance should be considered for sustainable applications.