Wire and arc additive manufacturing (WAAM) is a 3D metal printing technique based on the arc welding process. WAAM is considered to be suitable to produce large-scale metallic components by combining high deposition rate and low cost. WAAM uses conventional welding consumable wires as feedstock. In some applications of steel components, one-off spare parts need to be made on demand from steel grades that do not exist as commercial welding wire. In this research, a specifically produced medium carbon steel (Grade XC-45), metal-cored wire, equivalent to a composition of XC-45 forged material, was deposited with WAAM to produce a thin wall. The specific composition was chosen because it is of particular interest for the on-demand production of heavily loaded aerospace components. The microstructure, hardness, and tensile strength of the deposited part were studied. Fractography studies were conducted on the tested specimens. Due to the multiple thermal cycles during the building process, local variations in microstructural features were evident. Nevertheless, the hardness of the part was relatively uniform from the top to the bottom of the construct. The mean yield/ultimate tensile strength was 620 MPa/817 MPa in the horizontal (deposition) direction and 580 MPa/615 MPa in the vertical (build) direction, respectively. The elongation in both directions showed a significant difference, i.e., 6.4% in the horizontal direction and 11% in the vertical direction. Finally, from the dimple-like structures observed in the fractography study, a ductile fracture mode was determined. Furthermore, a comparison of mechanical properties between WAAM and traditionally processed XC-45, such as casting, forging, and cold rolling was conducted. The results show a more uniform hardness distribution and higher tensile strength of the WAAM deposit using the designed metal-cored wires.

The effects of single and double pulse resistance spot welding on the microstructures of an advanced high strength automotive steel are presented in this work. The double pulse welding schemes partially remelt the primary weld nugget and anneal the area at the fusion boundary of the nugget. The effects of the annealing treatment on the segregation and the microstructure have been studied by electron probe microanalysis (EPMA) in combination with electron backscatter diffraction (EBSD). Results show that phosphorus has been redistributed at the primary weld nugget edge of the double pulse welds, while the mean block width and ellipticity of the prior austenite grains were smaller in welds subjected to double pulsing compared with single pulse weld. A favourable failure mode was obtained for the double pulse welds although behaviour did not correlate with the measured grain size.

Laser powder bed fusion (L-PBF), categorized as additive manufacturing technique, has a capability to fabricate NiTi (Nitinol) shape memory alloys with tailorable functional properties and complex geometries. An important processing parameter, hatch distance (h), is often related to macroscale structural defects; however, its role on controlling the microstructure and functional properties is usually underestimated in L-PBF of NiTi. In this work, equiatomic NiTi (50.0 at% Ni) parts were fabricated with various hatch distances to tailor the microstructure and their shape memory characteristics. Contrary to what is observed in Ni-rich NiTi alloys, in this work, we demonstrate that phase transformation temperatures of L-PBF equiatomic NiTi do not decrease proportionally with hatch distance but rather relate to a critical hatch distance value. This critical value (120 μm) is derived from the synergistic effect of thermal stress and in situ reheating. Below this value, epitaxial grain growth and in situ recrystallization are enhanced, while above, irregular grains are formed and dislocations induced by thermal stresses decrease. However, the critical value found herein is characterized by high dislocation density and fine grain size, resulting in a superior thermal cyclic stability. The proposed finite element model is proven to be an effective tool to understand and predict the effect of hatch distance on grain morphology and dislocation density evolutions in L-PBF NiTi SMAs. In the present study, we provide a comprehensive understanding for in situ controlling L-PBF NiTi microstructure and functional characteristics, which contributes to designing 4-dimensional shape memory alloys.