W alloys are currently widely studied materials for their potential application in future fusion reactors. In the presented study, we report on the preparation and properties of mechanically alloyed W-Ti powders compacted by pulsed electric current sintering. Four different powder compositions of W-(3%–7%)Ti with Hf or HfC were prepared. The alloys’ structure contains only high-melting-point phases, namely the W-Ti matrix, complex carbide (Ti,W,Hf)C and HfO₂ particle dispersion; Ti in the form of a separate phase is not present. The bending strength of the alloys depends on the amount of Ti added. The addition of 3 wt. % Ti led to an increase whereas 7 wt. % Ti led to a major decrease in strength when compared to unalloyed tungsten sintered at similar conditions. The addition of Ti significantly lowered the room-temperature thermal conductivity of all prepared materials. However, unlike pure tungsten, the conductivity of the prepared alloys increased with the temperature. Thus, the thermal conductivity of the alloys at 1300 °C approached the value of the unalloyed tungsten.

In this work, CoCrNi, FeCoCrNi and CoCrFeMnNi concentrated alloys with a Y-Ti oxide particle dispersion were prepared by mechanical alloying and Spark Plasma Sintering. The alloy consists of an FCC Ni-based matrix with a Y-Ti oxide dispersion and additional phases of Cr₂₃C₆ and Cr₂O₃. The effect of Fe, Mn, and Y-Ti oxide particles on the formation of oxide scales and the composition of the adjacent CoCrNi and FeCoCrNi alloys was studied. It was found that alloys without Mn in their composition form a protective Cr₂O₃ scale. The Cr₂₃C₆ particles provide an alternative mechanism for balancing the chromium loss during the oxidation. Y and Ti from the oxide particles participate in the formation of the protective oxide scales. Fe promotes Y and especially Ti diffusion through the Cr₂O₃ scale, resulting in the formation of Ti-depleted regions in the alloy. The findings will serve for the further development of these new materials.

Metastable β-Ti alloy Ti-15Mo was prepared by cryogenic ball milling in a slurry of liquid argon. Material remained ductile even at low temperatures, which suppressed particle refinement, but promoted intensive plastic deformation of individual powder particles. Repetitive deformation of powder particles is similar to the multidirectional rolling and resembles bulk severe plastic deformation (SPD) methods. Initial and milled powders were compacted by spark plasma sintering. Sintered milled powder exhibited a refined microstructure with small β-grains and submicrometer sized α-phase precipitates. The microhardness and the yield tensile strength of the milled powder after sintering at 850 °C attained 350 HV and 1200 MPa, respectively. Low ductility of the material can be attributed to high oxygen content originating from the cryogenic milling. This pioneering work shows that cryogenic milling followed by spark plasma sintering is able to produce two-phase β-Ti alloys with refined microstructure and very high strength levels.