To meet the urgent need of society for advanced photocatalytic materials, novel visible light driven heterostructured composite was constructed based on graphitic carbon nitride (g-C₃N₄) and fibrous TiO₂. The g-C₃N₄/TiO₂ (CNT) composite was prepared through electrospinning technology and followed calcination process. The state of the g-C₃N₄ and fibrous TiO₂ was tightly coupled. The photocatalytic performance was measured by degrading the Rhodamine B. Compared to commercial TiO₂ (P25^®) and electrospun TiO₂ nanofibers, the photocatalytic performance of CNT composite was higher than them. The formation of CNT heterostructures and the enlarged specific surface area enhanced the photocatalytic performance, suppressing the recombination rate of photogenerated carriers while broadening the absorption range of light spectrum. Our studies have demonstrated that heterostructured CNT composite with an appropriate proportion can rational use of visible light and can significantly promote the photogenerated charges transferred at the contact interface between g-C₃N₄ and TiO₂.

Polyvinyl alcohol/poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PVA/PEDOT:PSS) composite ultrafine fibers were successfully fabricated by high pressure airflow assisted electrospinning. The electrical properties of PVA/PEDOT:PSS nanofibers with different diameters were characterized. The average diameter of the nanofibers can be down to 68 nm. Due to its large specific surface area, ammonia sensing of the ultrafine nanofibers is more sensitive than the traditional electrospun fibers (average fiber diameter of 263 nm). The ammonia sensing properties of the samples were tested by impedance analysis. The results show that ultrafine PVA/PEDOT:PSS nanofibers are more suitable for detecting low concentrations of ammonia with higher sensitivity.

Self-powered nanogenerators composed of poly(vinylidene fluoride) (PVDF) have received much attention. Solution blow spinning (SBS) is a neoteric process for preparing nanofiber mats with high efficiency and safely, and SBS is a mature fiber-forming technology that offers many advantages over conventional electrospinning methods. Herein, we adopted the SBS method to prepare independent PVDF nanofiber membranes (NFMs), and successfully employed them as nanogenerators. Finally, we tested the change in the output current caused by mechanical compression and stretching, and studied its durability and robustness by charging the capacitor, which can drive tiny electronic devices. The results show that the PVDF nanogenerators by using this SBS equipment can not only be used in wearable electronic textiles, but are also suitable for potential applications in micro-energy harvesting equipment.