Over the past decades, extensive studies on municipal solid waste incineration (MSWI) ashes have been performed to develop more effective recycling and waste management programs. Despite the large amount of research activities and the resulting improvements to MSWI ashes, the recycling programs for MSWI ashes are limited. For instance, although the U.S. generates more MSWI ashes than any other country in the world, its reuse/recycle programs are limited; bottom ash and fly ash are combined and disposed of in landfills. Reuse of MSWI ashes in the construction sectors (i.e., geomaterials, asphalt paving, and concrete products) as replacements for raw materials is one of most promising options because of the large consumption and relatively lenient environmental criteria. The main objective of this study was to comprehensively review MSWI ashes with regard to specific engineering properties and their performance as construction materials. The focus was on (1) the current practices of MSWI ash management (in particular, a comparison between European countries and the U.S.), (2) the engineering properties and performance of ashes when they are used as substitutes of construction materials and for field applications, and (3) the environmental properties and criteria for the use of MSWI ashes. Overall, the asphalt and concrete applications are the most promising, from both the mechanical and leachate viewpoints. However, cons were also observed: high absorption of MSWI ash requires a high asphalt binder content in hot-mix asphalt, and metallic elements in the ash may generate H₂ gas in the high-pH environment of the concrete. These side effects can be predicted via material characterization (i.e., chemical and physical), and accordingly, proper treatment and/or modified mix proportioning can be performed prior to use.

With the continuous research efforts, sophisticated predictive molecular dynamics (MD) models for C-S-H have been developed, and the application of MD simulation has been expanded from fundamental understanding of C-S-H to nano-engineered cement composites. This paper comprehensively reviewed the current state of MD simulation on calcium-silicate-hydrate (C-S-H) and its diverse applications to nano-engineered cement composites, including carbon-based nanomaterials (i.e., carbon nanotube, graphene, graphene oxide), reinforced cement, cement–polymer nanocomposites (with an application on 3D printing concrete), and chemical additives for improving environmental resistance. In conclusion, the MD method could not only compute but also visualize the nanoscale behaviors of cement hydrates and other ingredients in the cement matrix; thus, fundamental properties of C-S-H structure and its interaction with nanoparticles can be well understood. As a result, the MD enabled us to identify and evaluate the performance of new advanced nano-engineered cement composites.

This paper aims to investigate the effects of edge-oxidized graphene oxide nanoflakes (EOGO) on the mechanical properties and sorptivity of cement composites. The EOGO used in this study was produced by a mechanochemical process that assists the production of EOGO in large quantities at significantly reduced costs, enabling its practical use for infrastructure construction. The scope of this work includes the use of EOGO as an additive in cement composites, including cement paste and mortar. This study explores two mixing methods: The dry-mix method and the wet-mix method. The dry-mix method uses EOGO as dry powder in cement composites whereas the wet-mix method uses a water-dispersed solution (using a sonication process). Varied percentages of EOGO, ranging from 0.01% to 1.0%, were used for both methods. To evaluate the concrete durability, the effect of EOGO addition on sorptivity of the cement composites was investigated by performing total porosity and water sorptivity tests. It was found that 0.05% of EOGO is the optimum proportion to exert the highest strength in compressive and flexural strength tests. In addition, the dry-mix method is comparable to the wet-mix method (with dispersion of EOGO), thus more practical for field engineering applications.

This study experimentally investigates the effects of edge-oxidized graphene oxide (EOGO), which is a low-cost carbon-based nanomaterial, on fresh and hardened properties of normal portland cement concrete (PCC) and fiber-reinforced concrete (FRC). Interestingly, adding EOGO to normal concrete mixtures improves the workability of concrete. In this regard, EOGOs as an additive were applied to FRCs in order to improve FRCs’ low workability without losing mechanical enhancement due to EOGOs. Two fiber types of basalt fiber (BF) and steel fiber (SF) were used in this study. First, 0.05% of EOGO by the cement weight was mixed in basalt FRC (BFRC) mixture, which is 0.1% of the BF by the concrete volume. Second, considering the results of BFRC, 0.1% of EOGO was employed in steel FRC (SFRC) mixture with 1.0% of SF by the concrete volume. Testing was aimed at investigating the effects of EOGO on the workability and mechanical strengths of the FRC mixtures. The test results illustrate that the EOGO improves workability more than 100% in the SFRC mixture but about 20% in the BFRC mixture. The EOGO provides a slight increase of both compressive and flexural strengths for normal concrete and SFRC mixtures. In contrast, it was observed that the EOGO increases the flexural strength of SFRC in terms of initial crack generation and range of elastic behavior. The EOGO-SFRC required more than 30% of energy to reach the initial crack point than the SFRC mixture.