We demonstrate the efficient chemical vapor deposition synthesis of single-walled carbon nanotubes where the activity and lifetime of the catalysts are enhanced by water. Water-stimulated enhanced catalytic activity results in massive growth of superdense and vertically aligned nanotube forests with heights up to 2.5 millimeters that can be easily separated from the catalysts, providing nanotube material with carbon purity above 99.98%. Moreover, patterned, highly organized intrinsic nanotube structures were successfully fabricated. The water-assisted synthesis method addresses many critical problems that currently plague carbon nanotube synthesis.

By using an ionic liquid of 1-butyl-3-methylimidazolium bis(trifluoromethanesulfonyl)imide, we uniformly dispersed single-walled carbon nanotubes (SWNTs) as chemically stable dopants in a vinylidene fluoride-hexafluoropropylene copolymer matrix to form a composite film. We found that the SWNT content can be increased up to 20 weight percent without reducing the mechanical flexibility or softness of the copolymer. The SWNT composite film was coated with dimethyl-siloxane–based rubber, which exhibited a conductivity of 57 siemens per centimeter and a stretchability of 134%. Further, the elastic conductor was integrated with printed organic transistors to fabricate a rubberlike active matrix with an effective area of 20 by 20 square centimeters. The active matrix sheet can be uniaxially and biaxially stretched by 70% without mechanical or electrical damage. The elastic conductor allows for the construction of electronic integrated circuits, which can be mounted anywhere, including arbitrary curved surfaces and movable parts, such as the joints of a robot's arm.

Among all known materials, we found that a forest of vertically aligned single-walled carbon nanotubes behaves most similarly to a black body, a theoretical material that absorbs all incident light. A requirement for an object to behave as a black body is to perfectly absorb light of all wavelengths. This important feature has not been observed for real materials because materials intrinsically have specific absorption bands because of their structure and composition. We found a material that can absorb light almost perfectly across a very wide spectral range (0.2–200 μm). We attribute this black body behavior to stem from the sparseness and imperfect alignment of the vertical single-walled carbon nanotubes.

Supercapacitor electrodes fabricated from single-walled carbon nanotubes (SWNTs) are shown to be capable of durable operation at 4 V, exceeding the operating voltage limit of activated carbon electrodes (AC, 3 V), while delivering significantly higher energy and power (see figure). Dual exploitation of SWNTs as combined electrodes and current collectors is also explored.