We report on polarization-sensitive direct current photoresponse of nanographite films in a 532–4000 nm spectral range. It is found that irradiation of the nanographite by the nanosecond laser pulses produces the electric current with intensity depending on the incidence angle and polarization of the laser beam. The obtained dependencies of the photoresponse on wavelength and polarization of excitation laser beam are discussed in terms of the surface photogalvanic and photon drag effects.

We present observations of the optical rectification effect in the nanocarbon film, which is excited by nanosecond pulses of a Nd:YAG laser in the absence of an external electric field. Effective second order susceptibility of the film material is found to be ${10}^{\text{−6}}$ CGSE, which is higher than that of conventional noncentrosymmetric crystals. The measured ratio of the dc voltage to the laser power is 500 and 650 mV/MW at the wavelengths of 1064 and 532 nm, respectively. This makes the nanocarbon materials a promising alternative to conventional semiconductor-based terahertz radiation sources.

The nonlinear scattering of light under the conditions of optical limiting of nanosecond pulsed laser radiation at a wavelength of 1064 nm in a nanodiamond (ND) hydrosol has been experimentally...

We report on the optical limiting (OL) in stable aqueous suspensions of detonation nanodiamond (ND) clusters with average size of 50, 110, and 320 nm. The nanosecond $Z$-scan measurements at wavelength of 532 nm revealed that the larger the cluster size, the better the OL performance and the higher the ray stability of the ND suspension. Our analysis showed that the nonlinear scattering and the nonlinear absorption are the dominant mechanisms of OL in aqueous ND suspensions.