In this study, the electromagnetic interference (EMI) shielding effectiveness (SE) of polymer composites based on natural graphite in flakes (NGF) and silicone rubber was investigated with the aim to contribute to the development of the technology of electromagnetic shielding materials. This topic has attracted great attention to the aeronautical and aerospace applications, due to the serious problems that EMI can cause to the functioning of electronic devices. According to this, the present work has produced samples of composite materials with variations on the sizes of the filler particles and composition of the samples. The electromagnetic characterization of the samples is given by the Vector Network Analyzer (VNA) in the X-band frequency range (8.2 – 12.4 GHz). The results indicate that the variation of particle sizes is determinant to the SE performance along with the X-band frequency range. Furthermore, the expansion of the range of granulometry allows controlling the curves of the peaks along the X-band.

In this manuscript, the electromagnetic wave absorption properties of sustainable porous carbon composites were evaluated over the X-band frequency range (8.2 - 12.4 GHz). The porous carbon material was made from the byproduct of cellulose production and was used as additive on the development of radar absorbing material (RAM) composites. These porous carbon materials have different characteristics, such as porosity size (180 µm < Ø₁ < 250 µm and 425 µm < Ø₂ < 500 µm) and particle size (ϕ₁ < 250 µm and 250 µm < ϕ₂ < 425 µm). Composite materials were also studied as frequency selective surface (FSS) structures. It was shown how complex permittivity and reflection loss (RL) can be manipulated over the frequency range using FSS structure. While regular RAM presented RL of 19 dB at ~11.8 GHz, FSS structure presented a RL of 19 dB shifted to 12.4 GHz regarding the same carbon porous material (with particles between 250 and 425 µm and porosity between 180 and 250 µm). It was demonstrated here the potential use of sustainable porous carbon as RAM, and how FSS structure can be used to tune the frequency of the RL maximum peak.