The insufficient osteogenesis and osseointegration of porous titanium based scaffold limit its further application. Early angiogenesis is important for scaffold survival. It is necessary to develop a multifunctional surface on titanium scaffold with both osteogenic and angiogenic properties. In this study, a biofunctional magnesium coating is deposited on porous Ti6Al4V scaffold. For osseointegration and osteogenesis analysis, in vitro studies reveal that magnesium-coated Ti6Al4V co-culture with MC3T3-E1 cells can improve cell proliferation, adhesion, extracellular matrix (ECM) mineralization and ALP activity compared with bare Ti6Al4V cocultivation. Additionally, MC3T3-E1 cells cultured with magnesium-coated Ti6Al4V show significantly higher osteogenesis-related genes expression. In vivo studies including fluorochrome labeling, micro-computerized tomography and histological examination of magnesium-coated Ti6Al4V scaffold reveal that new bone regeneration is significantly increased in rabbits after implantation. For angiogenesis studies, magnesium-coated Ti6Al4V improve HUVECs proliferation, adhesion, tube formation, wound-healing and Transwell abilities. HUVECs cultured with magnesium-coated Ti6Al4V display significantly higher angiogenesis-related genes (HIF-1α and VEGF) expression. Microangiography analysis reveal that magnesium-coated Ti6Al4V scaffold can significantly enhance the blood vessel formation. This study enlarges the application scope of magnesium and provides an optional choice to the conventional porous Ti6Al4V scaffold with enhanced osteogenesis and angiogenesis for further orthopedic applications.

Microfabrication based on photopolymerization is typically achieved by scanning a focal spot within the material point by point, which significantly limits fabrication speed. In this paper, we explore a method for rapid fabrication of high-aspect-ratio microstructures based on photopolymerization using a femtosecond laser beam that is converted into a Bessel beam by an axicon. With stationary exposure, a polymer fiber measured at 200 μm in length and 400 nm in width (500∶1 aspect ratio) was fabricated within 50 ms of exposure time. The exposure conditions can be adjusted to produce fibers with variable widths. A phenomenological polymerization-threshold model is adapted for Bessel-beam exposure. The revised model is applied to analyze the structure width and estimate the order of multi-photon absorption. Examination of the cross section of the fibers shows that they are nearly monolithic, suggesting that active species diffuse during photopolymerization. By scanning the Bessel beam in the plane transverse to the direction of beam propagation, mesh structures are fabricated with a single-pass scan, showing the potential of this method for rapid fabrication of large-scale high-aspect-ratio microstructures for applications in photonics, micro-machines, and tissue engineering.

Polyetheretherketone (PEEK) is an alternative biomedical polymer material to traditional metal and ceramic biomaterials. However, as a bioinert material, its wide application in the medical field is seriously restricted due to its lack of bioactivity. In this research, pure Mg was successfully deposited on a PEEK substrate by vapor deposition to improve the antibacterial properties of PEEK implants. The morphology and elemental composition of the coating were characterized by scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS). The higher the deposition temperature, the larger the Mg particle size. The Mg coating possesses a hydrophilic surface and a higher surface free energy that create its good biocompatibility. The Mg coating on a PEEK substrate withstands up to 56 days’ immersion. The antibacterial test showed that the antibacterial rate of coated PEEK is 99%. Mg-coated PEEK demonstrates promising antibacterial properties.

We report on the experimental and theoretical studies of ultrafast laser-induced optical breakdown on the surface of fused silica to elucidate the mechanism of damage formation and sub-optical-cycle dynamics in material processing using single and a burst of two femtosecond laser pulses. Ionization pathways, including photo-ionization (PI) and avalanche ionization (AI), are investigated by using single-beam and double-beam laser damage threshold measurements, which are used to analyze electron dynamics and extract the avalanche coefficient. The relationship between damage size and laser fluence is interpreted as a result of a combination of PI and AI. Electrical field rather than laser intensity is the fundamental influential factor in PI, and AI is found to play a significant role in creating the free electron density needed for optical breakdown. These findings are verified by a double-pulse delay-scan experiment where two cross-polarized pulses are used to induce damage with delay within a few optical cycles. Variation of the damage diameter is observed within one optical cycle, which is explained by the periodic change of polarization in the combined electric field. This finding shows the potential of controlling laser induced damage by tuning the temporal overlap of a burst of ultrashort laser pulses.

Thermosensitive nanogels are highly sensitive to temperature fluctuations, making precise thermal control critical for uniform particle formation and consistent product quality. This study introduces a TRIZ-guided reactor design that integrates material-level self-feedback heating with structurally homogenized heat transfer, shifting temperature regulation from conventional multi-point feedback to intrinsic physical adaptation. Experimental evaluation demonstrated that the optimized system reduced the maximum temperature difference from 6.5 °C to 3.2 °C and decreased the standard deviation from 3.9 °C to 1.8 °C, resulting in improved reaction stability. Correspondingly, monomer conversion increased from 90% to 95%, and the particle size distribution narrowed, with PDI decreasing from 0.32 to 0.18. The energy consumption per unit mass of reactant also decreased from 3.6 kJ·g⁻¹ to 2.5 kJ·g⁻¹. These results indicate that the TRIZ-based self-feedback approach effectively enhances temperature uniformity, reaction control, and energy efficiency, providing a transferable strategy for temperature-sensitive polymerization and nanomaterial synthesis.