Atmospheric plasma spray (APS) yttria-stabilized zirconia coatings have a complex microstructure with a variety of pores that significantly reduce the thermal conductivity. APS thermal barrier coatings (TBCs) with a similar monoclinic phase were prepared. The pore sizes and distributions of the coatings were obtained by scanning their cross-section via SEM; the scanned areas were over 1 mm × 2 mm and more than 23,000 pores for each coating were analyzed. Multiple linear regression was used to analyze the porosity data and then to determine the quantitative relationship between different types of pores and thermal conductivity. Results revealed that the different pores have different effects on decreasing the thermal conductivity. The small, vertical pores have the biggest effect, while the horizontal pores also play a significant role in decreasing the thermal conductivity.

In this paper, the effect of microstructure on the thermal conductivity of plasma-sprayed Y₂O₃ stabilized ZrO₂ (YSZ) thermal barrier coatings (TBCs) is investigated. Nine freestanding samples deposited on aluminum alloys are studied. Cross-section morphology such as pores, cracks, m-phase content, grain boundary density of the coated samples are examined by scanning electron microscopy (SEM) and electron back-scattered diffraction (EBSD). Multiple linear regressions are used to develop quantitative models that describe the relationship between the particle parameters, m-phase content and features of the microstructure such as porosity, crack-porosity, and the length density of small and big angle-cracks. Moreover, the relationship between the microstructure and thermal conductivity is investigated. Results reveal that the thermal conductivity of the coating is mainly determined by the microstructure and grain boundary density at room temperature (25 °C), and by the length density of big-angle-crack, monoclinic phase content and grain boundary density at high temperature (1200 °C).