Hot-rolled backup rolls are widely used in steel rolling and usually need to be repaired by arc hardfacing after becoming worn. However, a corrugated-groove defect commonly occurs on the roll surface due to the uneven hardness distribution in the hardfacing layers, affecting the proper usage of the roll. Accordingly, a new swing-arc submerged arc welding (SA-SAW) process is proposed to attempt to solve this drawback. The microstructure and hardness are then investigated experimentally for both SAW and SA-SAW hardfacing layers. It is revealed that a self-tempering effect occurs in the welding pass bottom and the welding pass side neighboring the former pass for both processes, refining the grain in the two areas. In all the zones, including the self-tempering zone (STZ), heat-affected zone (HAZ), and not-heat-affected zone in the welding pass, both SAW and SA-SAW passes crystallize in a type of columnar grain, where the grains are the finest in STZ and the coarsest in HAZ. In addition, the arc swing improves the microstructure homogeneity of the hardfacing layers by obviously lowering the tempering degree in HAZ while promoting the even distribution of the arc heat. Accordingly, the hardness of the SA-SAW bead overall increases and distributes more uniformly with a maximum difference of < 80 HV_0.5 along the horizontal direction of the bead. This hardness difference in SA-SAW is accordingly decreased by ~38.5% compared to that of the SAW bead, further indicating the practicability of the new process.

To solve the problems of poor weld formation, difficult slag removal, and inferior joint microstructure and hardness in conventional narrow-gap submerged arc welding (NG-SAW), a swing arc NG-SAW process assisted by pre-embedding cold wires was proposed. Synergistically optimizing the welding energy parameters and additional cold wires ensured sound weld formation and enhanced slag detachability, while the efficiency of multilayer welding was improved by reducing the number of weld layers by 33.3%. The slag adhesion mechanism is clarified as follows: a high welding heat input facilitates elemental diffusion at the weld–slag interface, leading to the formation of a continuous and thick interlayer composed of (Fe,Mn)O and MgO-Al₂O₃-CaO phases. This interlayer strengthens the chemical bonding between slag and weld, thereby impeding slag removal. Microstructure evolution analysis of the multilayer welded joint revealed that the variable-angle design increases the groove volume and, combined with the heat-absorbing effect of the additional wires, accelerates molten pool cooling, thereby refining grains in both the weld metal zone and reheat-affected zone. Meanwhile, the tempering exerted by the heat-affected zone (HAZ) of the subsequent weld layer on the previous layer is attenuated. This promotes the gradual transformation of hard-brittle lath martensite in the coarse-grained heat-affected zone (CGHAZ) of the bottom layer into tougher tempered martensite/bainite in the CGHAZ of the upper layers. As a result, the hardness uniformity within the HAZ, the critical weak region of the joint, was enhanced by 54%, enabling synchronous improvement in microstructural homogeneity, hardness distribution, and overall welding efficiency.