Nowadays, the self-healing approach in materials science mainly relies on functionalized polymers used as matrices in nanocomposites. Through different physicochemical pathways and stimuli, these materials can undergo self-repairing mechanisms that represent a great advantage to prolonging materials service-life, thus avoiding early disposal. Particularly, the use of the Joule effect as an external stimulus for self-healing in conductive nanocomposites is under-reported in the literature. However, it is of particular importance because it incorporates nanofillers with tunable features thus producing multifunctional materials. The aim of this review is the comprehensive analysis of conductive polymer nanocomposites presenting reversible dynamic bonds and their energetical activation to perform self-healing through the Joule effect.

The intrinsic self-healing ability of polyketone (PK) chemically modified into furan and/or OH groups containing derivatives is presented. Polymers bearing different ratios of both functional groups were cross-linked via furan/bis-maleimide (Diels-Alder adducts) and hydrogen bonding interactions (aliphatic and aromatic OH groups). The resulting thermosets display tuneable softening points (peak of tan (δ)) from 90 to 137 °C as established by DMTA. It is found that the cross-linked system containing only furan groups shows the highest softening temperature. On the other hand, systems displaying the combination of Diels-Alder adducts and hydrogen bonding (up to 60 mol % of -OH groups) do not show any change in modulus between heating cycles (i.e. factually a quantitative recovery of the mechanical behaviour). It is believed that the novelty of these tuneable thermosets can offer significant advantages over conventional reversible covalent systems. The synergistic reinforcement of both interactions resists multiple heating/healing cycles without any loss of mechanical properties even for thermally healed broken samples

Both shape memory and self-healing polymers have received significant attention from the materials science community. The former, for their application as actuators, self-deployable structures, and medical devices; and the latter, for extending the lifetime of polymeric products. Both effects can be stimulated by heat, which makes resistive heating a practical approach to trigger these effects. Here we show a conductive polyketone polymer and carbon nanotube composite with cross-links based on the thermo-reversible furan/maleimide Diels–Alder chemistry. This approach resulted in products with efficient electroactive shape memory effect, shape reprogrammability, and self-healing. They exhibit electroactive shape memory behavior with recovery ratios of about 0.9; requiring less than a minute for shape recovery; electroactive self-healing behavior able to repair microcracks and almost fully recover their mechanical properties; requiring a voltage in the order of tens of volts for both shape memory and self-healing effects. To the best of our knowledge, this is the first report of electroactive self-healing shape memory polymer composites that use covalent reversible Diels–Alder linkages, which yield robust solvent-resistant polymer networks without jeopardizing their reprocessability. These responsive polymers may be ideal for soft robotics and actuators. They are also a step toward sustainable materials by allowing an increased lifetime of use and reprocessability.

In this work, we prepared electrically conductive self-healing nanocomposites. The material consists of multi-walled carbon nanotubes (MWCNT) that are dispersed into thermally reversible crosslinked polyketones. The reversible nature is based on both covalent (Diels-Alder) and non-covalent (hydrogen bonding) interactions. The design allowed for us to tune the thermomechanical properties of the system by changing the fractions of filler, and diene-dienophile and hydroxyl groups. The nanocomposites show up to 1 × 10⁴ S/m electrical conductivity, reaching temperatures between 120 and 150 °C under 20–50 V. The self-healing effect, induced by electricity was qualitatively demonstrated as microcracks were repaired. As pointed out by electron microscopy, samples that were already healed by electricity showed a better dispersion of MWCNT within the polymer. These features point toward prolonging the service life of polymer nanocomposites, improving the product performance, making it effectively stronger and more reliable.

Exfoliated graphite (ExG) embedded in a polymeric matrix represents an accessible, cost-effective, and sustainable method for generating nanosized graphite-based polymer composites with multifunctional properties. This review article analyzes diverse methods currently used to exfoliate graphite into graphite nanoplatelets, few-layer graphene, and polymer-assisted graphene. It also explores engineered methods for small-scale pilot production of polymer nanocomposites. It highlights the chemistry involved during the graphite intercalation and exfoliation process, particularly emphasizing the interfacial interactions related to steric repulsion forces, van der Waals forces, hydrogen bonds, π-π stacking, and covalent bonds. These interactions promote the dispersion and stabilization of the graphite derivative structures in polymeric matrices. Finally, it compares the enhanced properties of nanocomposites, such as increased thermal and electrical conductivity and electromagnetic interference (EMI) shielding applications, with those of neat polymer materials.

This study examines the preparation of electrically conductive polymer networks based on furan-functionalised polyketone (PK-Fu) doped with multi-walled carbon nanotubes (MWCNTs) and reversibly crosslinked with bis-maleimide (B-Ma) via Diels-Alder (DA) cycloaddition. Notably, the incorporation of 5 wt.% of MWCNTs results in an increased modulus of the material, and makes it thermally and electrically conductive. Analysis by X-ray photoelectron spectroscopy indicates that MWCNTs, due to their diene/dienophile character, covalently interact with the matrix via DA reaction, leading to effective interfacial adhesion between the components. Raman spectroscopy points to a more effective graphitic ordering of MWCNTs after reaction with PK-Fu and B-Ma. After crosslinking the obtained composite via the DA reaction, the softening point (tan(δ) in dynamic mechanical analysis measurements) increases up to 155 °C, as compared to the value of 130 °C for the PK-Fu crosslinked with B-Ma and that of 140 °C for the PK-Fu/B-Ma/MWCNT nanocomposite before resistive heating (responsible for crosslinking). After grinding the composite, compression moulding (150 °C/40 bar) activates the retro-DA process that disrupts the network, allowing it to be reshaped as a thermoplastic. A subsequent process of annealing via resistive heating demonstrates the possibility of reconnecting the decoupled DA linkages, thus providing the PK networks with the same thermal, mechanical, and electrical properties as the crosslinked pristine systems.