Fabrication of biocompatible electrodes for the investigation of catecholamines is a known challenge. In this work, methionine was chosen as a modifier for fabrication of a biocompatible carbon paste electrode by electropolymerization, through cyclic voltammetry. The electrochemical behavior of the poly(methionine) modified carbon paste electrode was characterized by cyclic voltammetry for simultaneous determination of dopamine (DA) and uric acid (UA) in a phosphate-buffered solution at pH 7.0. In the absence of an amino acid methionine layer, the bare carbon paste electrode exhibits rather poor voltammetric signals in DA and UA in the binary mixture, with oxidation potentials of DA and UA overlapping with each other. The poly(methionine) modified carbon paste electrode exhibits good catalytic activity with noticeably different oxidation potentials of DA and UA. The experimental results closely agree with the theoretical prediction based on a Fukui function complementary to the simulated electrostatic potential maps.

Thermochromic tungsten-doped VO₂ thin films were successfully fabricated using a W-V alloy target. X-ray diffraction analyses showed that the W-doped VO₂ film had a preferred orientation of (011), and that the doping did not degrade the film crystallinity compared with that of the pure film. X-ray photoelectron spectroscopy and energy-dispersive spectroscopy showed that the doped 0.81 atom% tungsten replaced vanadium in the lattice of the film. The metal–insulator transition temperature of the W-doped VO₂ film was reduced to 35.5 °C, which is close to room temperature. Additionally, the infrared transmittance modulation of the W-doped film at λ = 2500 nm reached 56%, indicating an excellent switching efficiency. The damage behavior of the W-doped VO₂ film under a femtosecond-laser irradiation was experimentally investigated. Our results revealed that defect-related damages induced by the femtosecond laser are relevant for W-doped VO₂ films. This study provides valuable insights into VO₂ films for potential applications in laser protection.

Ar/O plasma irradiation is proposed for post-treatment of vanadium dioxide (VO₂) films. Oxidation and surface migration were observed in the VO₂ films following irradiation. This combined effect leads to an effective stoichiometry refinement and microstructure reconstruction in the interfacial area. A notable improvement in luminous transmittance and an enhancement in phase transition performance of the treated VO₂ films were achieved. Compared with that of as-deposited VO₂ films, the electrical phase transition amplitude of treated films increased more than two-fold. The relative improvement in luminous transmittance (380–780 nm) is 47.4% (from 25.1% to 37%) and the increase in solar transmittance is 66.9% (from 29.9% to 49.9%), which is comparable to or better than the previous work using anti-reflection (AR) coatings or doping methods. The interfacial boundary state proved to be crucial and Ar/O plasma irradiation offers an effective approach for further refinement of thermochromic VO₂ films.