Ca deoxidation has been acknowledged recently as an effective oxide metallurgy technology that improves the toughness of the heat affected zone (HAZ) in high-strength low-alloy (HSLA) steel plates after large heat input welding. This paper describes the effect of Ca concentrations on the formation behavior of the non-metallic inclusions in the HAZs of a series of thick HSLA steel plates after large heat input welding at 400 kJ cm⁻¹. The quantitative statistics on the inclusions show that the Ca addition significantly decreases the quantity of the pure MnS sulfide, but increases that of the complex oxysulfide. The pure MnS sulfide precipitates below the solidus temperature, while the complex oxysulfide forms in the molten liquid, leading to the core (oxide) and shell (sulfide) structure. The Ca addition proportionally improves the HAZ toughness of these thick HSLA steel plates, primarily owing to the positive effect of the complex oxysulfides on the refinement of the HAZ microstructure.

In the present study, the mechanism of improving HAZ toughness of steel plate with Mg deoxidation after the simulated welding with the heat input of 400 kJ/cm was investigated through in situ observation, characterization with SEM-EDS and TEM-EDS, and thermodynamic calculation. It was found that intragranular acicular ferrite (IAF) and polygonal ferrite (PF) contributed to the improvements of HAZ toughness in steels with Mg deoxidation. With the increase of Mg content in steel, the oxide in micron size inclusion was firstly changed to MgO-Ti₂O₃, then to MgO with the further increase of Mg content in steel. The formation of nanoscale TiN particles was promoted more obviously with the higher Mg content in the steel. The growth rates of austenite grains at the high-temperature stage (1400~1250 °C) during the HAZ thermal cycle of steels with conventional Al deoxidation and Mg deoxidation containing 0.0027 and 0.0099 wt% Mg were 10.55, 0.89, 0.01 μm/s, respectively. It was indicated that nanoscale TiN particles formed in steel with Mg deoxidation were effective to inhibit the growth of austenite grain. The excellent HAZ toughness of steel plates after welding with a heat input of 400 kJ/cm could be obtained by control of the Mg content in steel to selectively promote the formation of IAF or retard the growth of austenite grain.

The characteristics of inclusions and microstructure in heat-affected zones (HAZs) of steel plates with Ca deoxidation after high heat input welding of 400 kJ·cm⁻¹ were investigated through simulated welding experiments and inclusions automatic analyzer systems. Typical inclusions in HAZs of steels containing 11 ppm and 27 ppm Ca were recognized as complex inclusions with the size in the range of 1~3 μm. They consisted of central Al₂O₃ and peripheral CaS + MnS with TiN distributing at the edge (Al₂O₃ + CaS + MnS + TiN). With increasing Ca content in steel, the average size of inclusions decreased from 2.23 to 1.46 μm, and the number density increased steadily from 33.7 to 45.0 mm⁻². Al₂O₃ + CaS + MnS + TiN complex inclusions were potent to induce the formation of intragranular acicular ferrite (IAF). Therefore, the HAZ toughness of steel plates after high heat input welding was improved significantly by utilizing oxide metallurgy technology with Ca deoxidation.