α-MoO ₃ is demonstrated as a mid-infrared biaxial hyperbolic crystal supporting in-plane phonon polaritons with concave wavefronts.

2D van der Waals (vdW) layered polar crystals sustaining phonon polaritons (PhPs) have opened up new avenues for fundamental research and optoelectronic applications in the mid‐infrared to terahertz ranges. To date, 2D vdW crystals with PhPs are only experimentally demonstrated in hexagonal boron nitride (hBN) slabs. For optoelectronic and active photonic applications, semiconductors with tunable charges, finite conductivity, and moderate bandgaps are preferred. Here, PhPs are demonstrated with low loss and ultrahigh electromagnetic field confinements in semiconducting vdW α‐MoO₃. The α‐MoO₃ supports strong hyperbolic PhPs in the mid‐infrared range, with a damping rate as low as 0.08. The electromagnetic confinements can reach ≈λ₀/120, which can be tailored by altering the thicknesses of the α‐MoO₃ 2D flakes. Furthermore, spatial control over the PhPs is achieved with a metal‐ion‐intercalation strategy. The results demonstrate α‐MoO₃ as a new platform for studying hyperbolic PhPs with tunability, which enable switchable mid‐infrared nanophotonic devices.

Hexagonal AlN (h-AlN) nanowires with an average diameter of around 15 nm have been prepared by an extended vapor–liquid–solid growth technique and characterized by X-ray diffraction, transmission electron microscopy, energy dispersive X-ray analysis, Raman spectroscopy and field emission measurements. This preparation is a rather simple route for bulk fabrication of h-AlN nanowires. The promising field emission property observed for h-AlN nanowires points to the important application potential of this material.