This review explores additive manufacturing (AM) for refractory tungsten (W) and its alloys, highlighting the primary challenges and determining factors in the AM of pure W, W alloys and composites. The challenges mainly arise from W’s high melting point, low laser absorptivity, high thermal conductivity, high melt viscosity, high oxygen affinity, high ductile-to-brittle transition temperature, and inherent embrittlement, which lead to defects and anomalies in AM-produced parts. This review focuses on both processes and alloying strategies to address the issues related to densification, micro-cracking, and the resultant properties in W-based components. Cracking in additively manufactured W remains a persistent issue due to thermal stress, embrittlement, and oxide formation. Powder characteristics, process parameters, and thermal management strategies are crucial for W densification. Throughout the review, existing knowledge and insights are organized into comprehensive tables, serving as valuable resources for researchers delving deeper into this topic. Future research in W-AM should focus on understanding the interaction between AM process parameters and microstructural and material design. Advances in atomic-level understanding, thermodynamic modeling, and data analytics have the potential to significantly enhance the precision, sustainability, and applicability of W-AM.

In this study, faceted TiO₂, predominately exposed with {010} facets (T-{010}), was synthesized with a two-step hydrothermal reaction and used for the degradation of acetaminophen (ACE) in an aqueous solution. T-{010} showed considerable photocatalytic reactivity, and its easy-settling (gravity-settling, ~97% of T-{010} settled after 30 min) property demonstrated acceptable reusability. A solid-state chemical reduction approach (NaBH₄) at a mild temperature (300 °C) was used for generation of an oxygen vacancy in T-{010} and P25 (commercial TiO₂). The oxygen vacancy concentrations of the samples were investigated by electron paramagnetic resonance (EPR). It was also found that NaBH₄ reduction induced the generation of both surface and subsurface Ti³⁺ on colored P25, but only surface Ti³⁺ species were formed on colored T-{010}. The prepared colored TiO₂ samples were successfully used for photocatalytic degradation of ACE in an aqueous solution under visible light illumination.