In this study, activated carbon (AC) from coconut shell, as a widely available agricultural waste, was synthesised in a simple one-step procedure and used to produce a magnetic Fe₃O₄/AC/TiO₂ nano-catalyst for the degradation of methylene blue (MB) dye under UV light. Scanning electron microscopy revealed that TiO₂ nanoparticles, with an average particle size of 45 to 62 nm, covered the surface of the AC porous structure without a reunion of its structure, which according to the TGA results enhanced the stability of the photocatalyst at high temperatures. The photocatalytic activities of synthesised AC, commercial TiO₂, Fe₃O₄/AC, and Fe₃O₄/AC/TiO₂ were compared, with Fe₃O₄/AC/TiO₂ (1:2) exhibiting the highest catalytic activity (98%). Furthermore, evaluation of the recovery and reusability of the photocatalysts after treatment revealed that seven treatment cycles were possible without a significant reduction in the removal efficiency.

Bimetallic gold-silver nanoparticles as unique catalysts were prepared using seed colloidal techniques. The catalytic capabilities of the nanoparticles were ascertained in the reduction of 4-nitrophenol to 4-aminophenol in the presence of sodium borohydride. Our results clearly showed that the rate of 4-NP reduction to 4-AP increased with a corresponding decrease in the diameter of the bimetallic NPs. The Au-Ag nanoparticles prepared with 5.0 mL Au seed volume indicated higher reduction activity, which was approximately 1.2 times higher than that of 2.0 mL Au seed volume in the reductive conversion of 4-NP to 4-AP. However, the monometallic NPs showed relatively less catalytic activity in the reductive conversion of 4-NP to 4-AP compared to bimetallic Au-Ag nanoparticles. Our studies also reinforced the improved catalytic properties of the bimetallic Au-Ag nanoparticles structure with a direct impact of the size or diameter and relative composition of the bimetallic catalytic nanoparticles.