The effect of hydrostatic pressure and cation type on chloride ion transport in marine underwater concrete cannot be ignored. The study of the chloride ion transport behavior of concrete under the effect of hydrostatic pressure and cation type coupling can provide a basis for durability design and the protection of marine concrete. In this work, the chloride ion transport behavior of marine concrete in four common chloride salt solutions under different hydrostatic pressures is studied by a hydrostatic pressure test device developed by the authors. The results show that hydrostatic pressure and its action time significantly influence the chloride ion transport behavior in marine concrete; the higher the hydrostatic pressure of concrete, the faster the chloride ion transport rate. The longer the time, the more chloride ions accumulated in the same position, and the farther the chloride ion transport distance. Cation type has a certain influence on the transport process of chloride ions. Under the same test conditions, the chloride ion transport rate in a divalent cation solution is about 5% higher than that in a monovalent cation solution. The results also show that the chloride ion binding capacity under hydrostatic pressure is only 10~20% of that under natural diffusion. Using the test results, a predictive model of a chloride ion apparent transport coefficient based on the hydrostatic pressure and hydrostatic pressure action time corrected by a cation type influence coefficient is established.

Mica is a harmful substance in sand and occurs frequently. The application of super standard mica sand is a difficult problem in large-scale engineering. In this work, the effects of an interface modifier, mineral admixture, and a curing system on the properties of cement-based materials with super standard mica sand were studied. The strength of cement-based materials linearly decreases with the mica content in sand. When the mica content in sand exceeds 6%, the compressive strength of mortar and concrete at 28 d decreases by more than 22.3% and 33.5%, respectively. By adding the silane coupling agent (SCA) of 50% mica mass and curing in natural conditions, the compressive strength of mortar increases by 10.9%. The cement-based materials with the SCA are more suitable for curing in natural conditions, and the performance of the SCA will not be affected by adding appropriate amounts of mineral admixture. The drying shrinkage strain of the concrete, with the sand containing high mica content modified by SCA, is reduced by 10.5%, and the diffusion of chloride ions in concrete is reduced. The XRD results show that the addition of the interfacial agent does not change the hydration products. The MIP and SEM results show that the SCA can form a bridge structure between the hydration products and the mica, improve the bonding strength of the interface zone, and reduce the number of harmful pores.