The high-theoretical-capacity (∼170 mAh/g) Prussian white (PW), Na_xFe[Fe(CN)₆]_y·nH₂O, is one of the most promising candidates for Na-ion batteries on the cusp of commercialization. However, it has limitations such as high variability of reported stable practical capacity and cycling stability. A key factor that has been identified to affect the performance of PW is water content in the structure. However, the impact of airborne moisture exposure on the electrochemical performance of PW and the chemical mechanisms leading to performance decay have not yet been explored. Herein, we for the first time systematically studied the influence of humidity on the structural and electrochemical properties of monoclinic hydrated (M-PW) and rhombohedral dehydrated (R-PW) Prussian white. It is identified that moisture-driven capacity fading proceeds via two steps, first by sodium from the bulk material reacting with moisture at the surface to form sodium hydroxide and partial oxidation of Fe²⁺ to Fe³⁺. The sodium hydroxide creates a basic environment at the surface of the PW particles, leading to decomposition to Na₄[Fe(CN)₆] and iron oxides. Although the first process leads to loss of capacity, which can be reversed, the second stage of degradation is irreversible. Over time, both processes lead to the formation of a passivating surface layer, which prevents both reversible and irreversible capacity losses. This study thus presents a significant step toward understanding the large performance variations presented in the literature for PW. From this study, strategies aimed at limiting moisture-driven degradation can be designed and their efficacy assessed.

Rechargeable sodium-ion batteries are the most attractive substitutes for lithium-ion batteries in large-scale energy storage devices due to wide spread reserves and low-cost of sodium resources and the similarities between sodium and lithium chemistry. However, finding a suitable cathode material is still a hurdle to be overcome. To date, Prussian white (PW), Na_xFe[Fe(CN)₆]_y·nH₂O has stood out as one of the most promising Na-host materials due to its low cost, facile synthesis and competitive electrochemical capacity. Despite this, there are concerns that this material will thermally decompose at relatively low temperatures to form cyanogen gas, which is a safety hazard. Thus, low vacancy Na_xFe[Fe(CN)₆]_y·nH₂O (x = 1.5, 1, 0.5 and 0) has been synthesized, and the influence of x on its thermal behavior systematically investigated. It is demonstrated that the thermal decomposition temperature, water content and moisture sensitivity of the samples strongly depend on the sodium content. The sample with x = 1.5 is found to be the most thermally stable and has the highest water content under the same experimental conditions. In addition, the sodium-rich samples (x = 1.5, 1 and 0.5) have higher surface water than the sodium-deficient one (x = 0). The local structure for this sample is also very different to the sodium-rich ones. Our findings offer new insights into the profound implications of proper material handling and safer operating conditions for practical Na-ion batteries and may be extended to analogous systems.