The equiatomic NiCrFeCoMn high-entropy alloy prepared by arc melting has a single crystallographic structure. Mechanical properties and microstructure of the NiCrFeCoMn high-entropy alloy deformed at high strain rates (900 s⁻¹ to 4600 s⁻¹) were investigated. The yield strength of the NiCrFeCoMn high-entropy alloy is sensitive to the change of high strain rates. Serration behaviors were also observed on the flow stress curves of the alloy deformed at the strain rates ranging from 900 s⁻¹ to 4600 s⁻¹. The Zerilli–Armstrong constitutive equation can be used to predict the flow stress curves of the NiCrFeCoMn high-entropy alloy. Large amounts of deformation bands led to obvious serration behaviors of the NiCrFeCoMn high-entropy alloy under dynamic loading.

The dynamic mechanical properties and microstructure of the (Al_0.5CoCrFeNi)_0.95Mo_0.025C_0.025 high entropy alloy (HEA) prepared by powder extrusion were investigated by a split Hopkinson pressure bar and electron probe microanalyzer and scanning electron microscope. The (Al_0.5CoCrFeNi)_0.95Mo_0.025C_0.025 HEA has a uniform face-centered cubic plus body-centered cubic solid solution structure and a fine grain-sized microstructure with a size of about 2 microns. The HEA possesses an excellent strain hardening rate and high strain rate sensitivity at a high strain rate. The Johnson–Cook plastic model was used to describe the dynamic flow behavior. Hat-shaped specimens with different nominal strain levels were used to investigate forced shear localization. After dynamic deformation, a thin and short shear band was generated in the designed shear zone and then the specimen quickly fractured along the shear band.