Thermal management remains a key challenge for lithium-ion batteries in electric vehicles, especially under transient driving and charging conditions. This study develops a coupled thermo-hydraulic model for a liquid-cooled battery thermal management system and uses it to compare four coolants with different thermophysical properties: water, ethylene glycol–water, propylene glycol–water, and Jet-A aviation fuel. Unlike studies that focus mainly on temperature reduction, the present work evaluates battery temperature, hydraulic pump power, and cooling load/heat rejection demand within the same framework. The coolants are tested under the FTP-75 driving cycle and a high-rate charging case while pump speed is varied between 1500 and 4500 rpm. Water provides the strongest cooling performance, reducing the battery temperature during FTP-75 from about 30 °C to 21.2 °C at 1500 rpm and 20.6–20.8 °C at 4500 rpm. During charging, water maintains the battery temperature near 23 °C at 1500 rpm, whereas ethylene glycol–water and Jet-A reach about 46–47 °C. Increasing pump speed improves thermal regulation, particularly for weaker-performing coolants, but it also increases auxiliary demand; for example, the RMS pump power of water during charging rises from 0.039 to 0.735 kW. Overall, the results show that coolant selection in liquid-cooled BTMS requires a balanced assessment of heat removal capability, pumping demand, and heat rejection requirements.

The development of sustainable, high-performance friction composites is critical for the automotive industry, given the environmental and health concerns associated with conventional brake pad materials such as asbestos and copper. This study investigates the effect of incorporating micro- and nano-sized Al₂O₃, SiC, and carbon nanotubes (CNTs) into a novel, eco-friendly, asbestos-free, and copper-free brake pad formulation. Six composite samples were fabricated via a cold-pressing and hot-molding process: five formulations containing a single, size-controlled micro-/nano-sized reinforcement (Al₂O₃, SiC, and CNTs), and one reference formulation (CBP# Reference) containing an unrefined, commercial-grade combination of Al₂O₃ and SiC in place of the size-controlled additive. All formulations were rigorously characterized for their physical, mechanical, and tribological properties. The nano-Al₂O₃ formulation exhibited the highest density (2.197 g/cm³) and compressive strength (249.7 MPa), while the micro-SiC formulation achieved superior wear resistance, recording the lowest weight loss (0.0053 g) and the highest hardness (90 HV). The nano-SiC formulation offered the most balanced overall performance, combining high hardness (86.2 HV) with the highest average friction force (33.65 N) and the most stable friction-time response among all samples. The CNT-reinforced formulation produced the highest maximum friction force (42.07 N) but showed only moderate improvement in density, hardness, and compressive strength relative to the ceramic-reinforced samples. Compared with the CBP# reference, all five developed formulations exhibited higher hardness and coefficient of friction alongside lower weight loss, confirming their potential as durable, sustainable alternatives for automotive brake friction applications.