Routine inspection is the most common form of highway bridge inspection to satisfy the requirements of the National Bridge Inspection Standards. The accuracy and reliability of documentation generated during these inspections are critical to the allocation of Department of Transportation construction, maintenance, and rehabilitation resources. Routine inspections are typically completed using only the visual inspection technique and rely heavily on subjective assessments made by bridge inspectors. In light of this, and given the fact that visual inspection may have other limitations that influence its reliability, the Federal Highway Administration initiated an investigation to examine the reliability of visual inspection as it is currently applied to bridges in the United States. This paper will summarize results from this study related to the accuracy and reliability of routine inspection documentation. A number of important conclusions were developed from the experimental study. Generally, it was found...

Significant recent advancements in cement-based, fiber-reinforced composite materials have stretched the bounds of concrete into the realm of ultrahigh-performance concrete (UHPC). The durability of a commercially available UHPC was independently evaluated through six standardized durability tests and the results are reported herein. Regardless of the curing treatment applied, this concrete exhibits significantly enhanced durability properties as compared to normal and high performance concretes. The concrete exhibited minimal damage after being subjected to two times the normal number of ASTM C 666 freeze–thaw cycles. It was innocuous to ASTM C 1260 ASR deterioration, to ASTM C 672 scaling deterioration, and to AASHTO T259 chloride penetration. The ASTM C 1202 Electrical Indication of Concrete’s Ability to Resist Chloride Ion Penetration test result was negligible if any steam-based curing treatment was applied, and was very low otherwise. Steam-based curing treatments significantly enhanced the ASTM C 9...

The flexural behavior of an ultrahigh-performance concrete UHPC was investigated through the testing and related analysis of a full-scale prestressed I-girder. A 28 ksi 193 MPa compressive strength steel fiber reinforced concrete was used to fabricate an 80 ft 24.4 m long AASHTO Type II girder containing 26 prestressing strands and no mild steel reinforcement. Intermediate and final behaviors, including cracking, flexural stiffness, and moment capacity, were investigated. Test results are compared to predictions based on standard analytical procedures. A relationship between tensile strain and crack spacing is developed. The uniaxial stress-strain response of UHPC when subjected to flexural stresses in an I-girder is determined and is verified to be representative of both the stress and flexural stiffness behaviors of the girder. A flexural design philosophy for this type of girder is proposed.