Biodegradable metal systems are the future of modern implantology. This publication describes the preparation of porous iron-based materials using a simple, affordable replica method on a polymeric template. We obtained two iron-based materials with different pore sizes for potential application in cardiac surgery implants. The materials were compared in terms of their corrosion rate (using immersion and electrochemical methods) and their cytotoxic activity (indirect test on three cell lines: mouse L929 fibroblasts, human aortic smooth muscle cells (HAMSC), and human umbilical vein endothelial cells (HUVEC)). Our research proved that the material being too porous might have a toxic effect on cell lines due to rapid corrosion.

This study investigates the damage behavior and surface integrity of chitosan–nanohydroxyapatite (CS/nHAp) composite coatings, along with their corrosion resistance and wettability, which directly affect their biological performance in vivo. The coatings were deposited on Ti13Zr13Nb and stainless steel using electrophoretic deposition (EPD) at various voltages and deposition times. Surface topography, morphology, composition, and roughness were characterized using microscopic techniques, while wettability, corrosion resistance, and mechanical properties were assessed. Three-point bending tests were performed to determine coating behavior under mechanical deformation. Hydrophilic, homogeneous CS/nHAp coatings were successfully deposited without visible cracks on the surface. Coatings deposited at 10 V exhibited higher corrosion potentials compared to uncoated titanium alloy. Mechanical testing showed that coatings deposited at 10 V were significantly harder than those deposited at 20 V. The CS/nHAp20_5 coating exhibited moderate hardness (0.33 ± 0.06 GPa), the lowest Young’s modulus (12.7 ± 1.4 GPa), increased flexibility, and good adhesion, without delamination during bending tests. These results demonstrate that by modifying deposition parameters, it is possible to adjust the mechanical and protective properties of CS/nHAp coatings for potential application of the developed coating in vascular stents.