Multimetallic neodymium–ytterbium–gadolinium compounds with 9-anthracenate and 9-acridinate anions were tested in order to create the first luminescent thermometer for elevated temperatures. High luminescence intensity and high signal resolution were reached thanks to the concentration quenching elimination due to the partial substitution of the emitting ions with Gd³⁺. As a result, NIR emitting materials for luminescence thermometry in the wide temperature range (83–393 K) based on lanthanide coordination compounds (CCs) were obtained. The best thermometric properties among the studied systems were demonstrated by Yb_0.02Nd_0.12Gd_0.86(ant)₃, and its temperature sensitivity reached 1.8% K⁻¹ in the temperature range of 293–393 K.

Two new VIS-excited NIR-emitting ytterbium complexes Yb(HPTC)(H₂O)₂ (Yb1) and Yb(HPTC)(Phen) (Yb2) were obtained. Both compounds demonstrated low toxicity for healthy and cancer cells, moreover Yb1 demonstrated selective accumulation in cancer cells.

Исследованы люминесцентные комплексы тербия и европия с тетрафтортерефталевой кислотой и фенантролином для применения в термометрии. Показано, что в отличие от смеси индивидуальных комплексов, демонстрирующих различную скорость фотодеградации, биметаллический комплекс сохраняет стабильное соотношение интенсивностей полос излучения Tb3+ и Eu3+ при общем снижении интенсивности люминесценции. Разработаны композитные материалы на основе синтезированных комплексов в полиимидных и полистирольных матрицах, сочетающие термочувствительные свой­ства с механической устойчивостью. Полученные результаты открывают перспективы создания стабильных люминесцентных термометров для биологических и микроэлектронных применений.