It is well known that the traditional synthetic polymers, such as Polyurethane foams, require raw materials that are not fully sustainable and are based on oil-feedstocks. For this reason, renewable resources such as biomass, polysaccharides and proteins are still recognized as one of the most promising approaches for substituting oil-based raw materials (mainly polyols). However, polyurethanes from renewable sources exhibit poor physical and functional performances. For this reason, the best technological solution is the production of polyurethane materials obtained through a partial replacement of the oil-based polyurethane precursors. This approach enables a good balance between the need to improve the sustainability of the polymer and the need to achieve suitable performances, to fulfill the technological requirements for specific applications. In this paper, a succinic-based polyol sample (obtained from biomass source) was synthesized, characterized and blended with cardanol-based polyol (Mannich-based polyol) to produce sustainable rigid polyurethane foams in which the oil-based polyol is totally replaced. A suitable amount of catalysts and surfactant, water as blowing reagent and poly-methylene diphenyl di-isocyanate as isocyanate source were used for the polyurethane synthesis. The resulting foams were characterized by means of infrared spectroscopy (FTIR) to control the cross-linking reactions, scanning electron microscopy (SEM) to evaluate the morphological structure and thermal gravimetric analysis (TGA) and thermal conductivity to evaluate thermal degradation behavior and thermal insulation properties.

Nowadays, the chemical industry is looking for sustainable chemicals to synthesize nanocomposite bio-based polyurethane foams, PUs, with the aim to replace the conventional petrochemical precursors. Some possibilities to increase the environmental sustainability in the synthesis of nanocomposite PUs include the use of chemicals and additives derived from renewable sources (such as vegetable oils or biomass wastes) which comprise an increasing wider base raw materials. Generally, sustainable PUs exhibit chemico-physical, mechanical and functional properties which are not comparable with those of PUs produced from petrochemical precursors. In order to enhance the performances as well as the bio-based aspect, the addition in the polyurethane formulation of renewable or natural fillers can be considered. Among these, walnut shells and cellulose are very popular wood-based waste and due to their chemical composition, carbohydrate, protein and/or fatty acid, can be used as reactive fillers in the synthesis of PUs, diatomite as natural inorganic nanoporous filler can be also evaluated to improve mechanical and thermal insulation properties of rigid PUs. In this respect, sustainable nanocomposite rigid PU foams are synthesized by using a cardanol-based Mannich polyol, MDI as isocyanate source, catalysts and surfactant to regulate the polymerization and blowing reactions, H2O as sustainable blowing agent and suitable amount (5wt%) of ultramilled walnut shell, cellulose and diatomite as filler. The effect of these fillers on the chemico-physical, morphological, mechanical and functional performances on PU foams has been analyzed.

The construction sector’s substantial contribution to global energy consumption and CO₂ emissions motivates the development of bio-based alternatives to fossil-derived rigid polyurethane (PUR) foam cores in structural sandwich panels. This study presents a comprehensive comparison of plywood sandwich panels manufactured with a rigid PUR foam containing a fast pyrolysis bio-oil (FPBO)-derived sugar polyol diluted with triethyl phosphate and panels of identical topology produced with a commercial reference PUR foam. In the bio-based formulation, a fraction of the sorbitol-based polyether polyol was replaced with the FPBO-derived sugar polyol. Both systems were characterized at the foam and panel levels for cellular microstructure, skeletal and envelope density, thermogravimetric stability, flammability, color, thermal conductivity and heat capacity, internal bond strength, compressive properties, and normal-incidence sound absorption and transmission loss. The newly developed foam exhibited similar skeletal density and porosity to the reference, comparable thermogravimetric stability with a slightly higher char residue, and lower thermal conductivity across the tested temperature range. Mechanical properties, including compressive strength, compressive modulus, and internal bond strength, showed minor reduction but remained within a comparable range. A distinct color change was observed, attributable to the presence of chromophoric constituents of the FPBO fraction. Overall, the results indicate that partial substitution of the fossil polyol with an FPBO-derived sugar polyol is technically feasible, yielding materials with comparable thermal, mechanical, or acoustic performance. No consistent performance advantage of either system was observed across the evaluated properties. The results support the potential of pyrolysis-derived bio-polyols for use in sustainable structural insulation products.