The degradation of polylactide (PLA) films of different structures under conditions of controlled composting has been studied. We have demonstrated that PLA underwent degradation within one month in a substrate that simulated standard industrial composting. Regardless of the initial structure of the samples, the number-average molecular weight (M_n) decreased to 4 kDa while the degree of crystallinity increased to about 70% after 21 days of composting. Addition of an inoculant to the standard substrate resulted in the accelerated degradation of the PLA samples for one week due to an abiotic hydrolysis. These findings have confirmed that industrial composting could solve the problem of plastic disposal at least for PLA.

Eight different types of tea bags were investigated in this work using dynamic light scattering, electrophoretic mobility and nanoparticle tracking analysis methods to determine the concentration and size of released particles from the bag materials at different temperatures and times. Infrared spectroscopy and calorimetric methods confirmed that the bag material consisted of synthetic (nylon or polypropylene) or natural polymers (cellulose). The size of the released particles lies in the range of 200 nm^–1 µm with an initial bimodal distribution and with an average diameter of about 600 nm. The concentration of released particles increases with increasing temperature and brewing time. The released particles of synthetic polymers remain quite stable and are not affected by natural enzymes, while cellulose particles are easily degraded by the proteolytic complex Morikrase. When analyzing the electrophoretic mobility, it was found that the released particles have a negative surface charge, which probably determines the absence of cytotoxicity established on the epithelial cell line Caco-2 even at the maximum values of the observed particle concentrations (14 × 10⁹ particle/L for synthetic polymers and 170 × 10⁹ particle/L for cellulose).

This study examines the nature of enzymatic degradation of polyethylene terephthalate (PET) films mediated by a novel recombinant LCC^ICCG PETase enzyme preparation based on P. verruculosum fungus. The investigation was conducted using amorphous PET samples and PET samples with varying degrees of crystallinity as substrates for PETase-catalyzed hydrolysis under different temperature and pH conditions. Mechanical testing revealed that enzymatic treatment reduced the yield stress by 20–25%, tensile strength by approximately twofold, and elongation at break by 5–10 times, while the deformation mechanism remained unchanged. Enzymatic degradation under acidic conditions was ineffective, whereas increasing the pH to 9–10 markedly accelerated PET degradation and the associated deterioration of mechanical properties. Thermal analysis (TGA, DSC) and microscopy (optical and scanning electron microscopy) demonstrated that degradation was localized at the polymer surface, leading to the formation of cavities, cracks, and submicron-sized pores rather than bulk material disintegration. An inverse correlation was observed between PET crystallinity and susceptibility to enzymatic degradation: samples with crystallinity below 13% could be almost completely degraded, whereas samples with crystallinity above 30% exhibited little or no measurable weight loss over the same period. Low-crystallinity PET underwent rapid degradation accompanied by a transient increase in crystallinity, while highly crystalline PET primarily accumulated surface defects that nevertheless caused a substantial loss of mechanical strength. Consequently, the experimental data obtained in this study provide useful information for understanding PET degradation and for future studies on enzymatic PET recycling. The systematization of feedstock characteristics and the elucidated patterns of enzymatic degradation will enable optimization of pretreatment, enzymatic hydrolysis, and monomer recovery process parameters, thereby facilitating the eventual production of secondary raw materials.