Grafting polyethylene glycol (PEG) onto a polymer’s surface is widely used to improve biocompatibility by reducing protein and cell adhesion. Although PEG is considered to be bioinert, its incorporation onto biomaterials has shown to improve cell viability depending on the amount and molecular weight (MW) used. This phenomenon was studied here by grafting PEG of three MW onto polyurethane (PU) substrata at three molar concentrations to assess their effect on PU surface properties and on the viability of osteoblasts and fibroblasts. PEG formed a covering on the substrata which increased the hydrophilicity and surface energy of PUs. Among the results, it was observed that osteoblast viability increased for all MW and grafting densities of PEG employed compared with unmodified PU. However, fibroblast viability only increased at certain combinations of MW and grafting densities of PEG, suggesting an optimal level of these parameters. PEG grafting also promoted a more spread cell morphology than that exhibited by unmodified PU; nevertheless, cells became apoptotic-like as PEG MW and grafting density were increased. These effects on cells could be due to PEG affecting culture medium pH, which became more alkaline at higher MW and concentrations of PEG. Results support the hypothesis that surface energy of PU substrates can be tuned by controlling the MW and grafting density of PEG, but these parameters should be optimized to promote cell viability without inducing apoptotic-like behavior.

In this study, textile fiber prototypes based on polyester and different Cu nanoparticles (CuNP) content were produced using melt-spinning to obtain bi-component multifilament fibers and melt-blowing to obtain non-woven fabrics. The prototypes were tested against pathogenic microorganisms such as S. aureus, E. coli, and C. albicans. It was shown that bi-component fibers offer excellent protection against pathogens, with up to 99% growth inhibition with 0.5% w/w for S. aureus and E. coli; meanwhile, non-woven fabric only shows activity against E. coli from 0.1% w/w of CuNP. Using different analytical techniques, it was possible to identify that the CuNP were confined exclusively in the outer cover of the bi-component fibers which may be associated with increased antimicrobial activity compared to the fibers in the non-woven fabric. The use of polymeric nanocomposites based on polyester/copper offers an alternative of great interest due to the versatility of the raw material and the high efficiency of copper nanoparticles as an antimicrobial additive.

BACKGROUND: Bovine bone matrix is a natural material that has been used in the treatment of bone lesions. In this study, bovine bone matrix Nukbone® (NKB) was investigated due its osteoconductive and osteoinductive properties. This biomaterial induces CBFA-1 activation and osteogenic differentiation, although the cytokines involved in these processes is still unknown. OBJECTIVE: The aim of this work was to determine the influence of NKB on the pro-osteoblastic and anti-osteoblastic cytokines secretion from human mesenchymal stem cells (hMSCs). METHODS: The hMSCs were cultured onto NKB and cytokines IL-2, IL-4, IL-6, IL-10, IL-12, IFN-γ and TNF-α were analized at 0-14 days by immunoassay. In addition, hemocompatibility of NKB and characterization of hMSCs were evaluated. RESULTS: NKB induces an increase on pro-osteoblastic cytokine secretion IL-4 and a decrease on anti-osteoblastic cytokine IL-6 secretion, at days 7 and 14 of cell culture. Interestingly, there was no statistical difference between secretion profiles of others cytokines analized. CONCLUSIONS: The up-regulation of IL-4 and down-regulation of IL-6, and the secretion profiles of other cytokines examined in this work, are findings that will contribute to the understanding of the role of NKB, and similar biomaterials, in bone homeostasis and in the osteoblastic differentiation of hMSCs.