Optimization of internal quantum efficiency (IQE) for InGaN quantum wells (QWs) light-emitting diodes (LEDs) is investigated. Staggered InGaN QWs with large electron-hole wavefunction overlap and improved radiative recombination rate are investigated for nitride LEDs application. The effect of interface abruptness in staggered InGaN QWs on radiative recombination rate is studied. Studies show that the less interface abruptness between the InGaN sub-layers will not affect the performance of the staggered InGaN QWs detrimentally. The growths of linearly-shaped staggered InGaN QWs by employing graded growth temperature grading are presented. The effect of current injection efficiency on IQE of InGaN QWs LEDs and other approaches to reduce dislocation in InGaN QWs LEDs are also discussed. The optimization of both radiative efficiency and current injection efficiency in InGaN QWs LEDs are required for achieving high IQE devices emitting in the green spectral regime and longer.

Staggered InGaN quantum wells (QWs) grown by metal-organic chemical vapor deposition are demonstrated as improved active region for visible light emitters. Theoretical studies indicate that InGaN QW with step-function-like In content in the quantum well offers significantly improved radiative recombination rate and optical gain in comparison to the conventional type-I InGaN QW. Experimental results of light emitting diode (LED) structure utilizing staggered InGaN QW show good agreement with theory. Polarization band engineering via staggered InGaN quantum well allows enhancement of radiative recombination rate, leading to the improvement of photoluminescence intensity and LED output power.

Strain-compensated InGaN-AlGaN quantum wells (QW) are investigated as improved active regions for lasers and light emitting diodes. The strain-compensated QW structure consists of thin tensile-strained AlGaN barriers surrounding the InGaN QW. The band structure was calculated by using a self-consistent 6-band kmiddotp formalism, taking into account valence band mixing, strain effect, spontaneous and piezoelectric polarizations, as well as the carrier screening effect. The spontaneous emission and gain properties were analyzed for strain-compensated InGaN-AlGaN QW structures with indium contents of 28%, 22%, and 15% for lasers (light-emitting diodes) emitting at 480 (500), 440 (450), and 405 nm (415 nm) spectral regimes, respectively. The spontaneous emission spectra show significant improvement of the radiative emission for strain-compensated QW for all three structures compared to the corresponding conventional InGaN QW, which indicates the enhanced radiative efficiency for light emitting diodes. Our studies show the improvement of the optical gain and reduction of the threshold current density from the use of strain-compensated InGaN-AlGaN QW as active regions for diode lasers.

The fabrication studies of silica/polystyrene (PS) colloidal microlens arrays with various aspect ratios were performed on the III-nitride light-emitting diodes (LEDs). The use of colloidal-based microlens arrays led to significant enhancement in light extraction efficiency for III-nitride LEDs. In varying the aspect ratios of the microlens arrays, the engineering of various PS thicknesses was employed by using high-temperature treatment and redeposition process. The effects of PS thickness on the light extraction efficiency and far-field emission patterns of InGaN quantum-well (QW) LEDs were studied. The total output powers of microlens LEDs with various PS thicknesses exhibited 1.93-2.70 times enhancement over that of planar LEDs, and the use of optimized PS layer thickness is important in leading the enhancement of the light extraction efficiency in large angular direction.