To clear away the harmful effects of the increment of electromagnetic pollution, high performance absorbers with appropriate impedance matching and strong attenuation capacity are strongly desired. In this study, a chain-like PPy aerogel decorated with MOF-derived nanoporous Co/C (Co/C@PPy) has been successfully prepared by a self-assembled polymerization method. With a filler loading ratio of 10 wt %, the composite of Co/C@PPy could achieve a promising electromagnetic absorption performance both in intensity and bandwidth. An optimal reflection loss value of −44.76 dB is achieved, and the effective bandwidth (reflection loss lower than −10 dB) is as large as 6.56 GHz. Furthermore, a composite only loaded with 5 wt % Co/C@PPy also achieves an effective bandwidth of 5.20 GHz, which is even better than numerous reported electromagnetic absorption (EA) materials. The result reveals that the as-fabricated Co/C@PPy—with high absorption intensity, broad bandwidth, and light weight properties—can be utilized as a competitive absorber.

In this study, Fe₃O₄/ZnO core–shell nanocomposites were synthesized through a chemical method of coating the magnetic core (Fe₃O₄) with ZnO by co-precipitation of Fe₃O₄ with zinc acetate in a basic medium of ammonium hydroxide. The phase structure, morphology and electromagnetic parameters of the Fe₃O₄/ZnO core–shell nanocomposites were investigated. The results indicated that the concentration of the solvent was responsible for controlling the morphology of the composites, which further influenced their impedance matching and microwave absorption properties. Moreover, Fe₃O₄/ZnO nanocomposites exhibited an enhanced absorption capacity in comparison with the naked Fe₃O₄ nanospheres. Specifically, the minimum reflection loss value reached −50.79 dB at 4.38 GHz when the thickness was 4.5 mm. It is expected that the Fe₃O₄/ZnO core–shell structured nanocomposites could be a promising candidate as high-performance microwave absorbers.

Currently, electromagnetic pollution management has gained much attention due to the various harmful effects on wildlife and human beings. Electromagnetic absorbers can convert energy from electromagnetic waves into thermal energy. Previous reports have demonstrated that reduced graphene oxide (rGO) makes progress in the electromagnetic absorption (EA) field. But the high value of permittivity of rGO always mismatches the impedance which results in more electromagnetic wave reflection on the surface. In this work, sandwich-like rGO/CuS/polypyrrole (PPy) nanoarchitectures have been synthesized by a facile two-step method. The experimental result has shown that a paraffin composite containing 10 wt.% of rGO/CuS/PPy could achieve an enhanced EA performance both in bandwidth and intensity. The minimum reflection loss (RL) value of −49.11 dB can be reached. Furthermore, the effective bandwidth can cover 4.88 GHz. The result shows that the as-prepared rGO/CuS/PPy nanoarchitectures will be a promising EA material.