Magnetic nanoparticles, such as Fe₃O₄ and Co₃O₄, play a vital role in the research on advanced microwave absorbing materials, even if problems such as high density and narrow band impedance matching are still unsolved. Herein, the study of lightweight hollow Fe₃O₄@reduced graphite oxide (RGO) nanocomposites synthesized via the solvothermal method is presented. The microstructure and crystal morphology of the materials were characterized by X-ray diffractometer (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) analyses. Single crystalline hollow Fe₃O₄ spheres were grown onto RGO flakes, leading to the formation of heterojunction, which further influenced the microwave absorption properties. The latter were evaluated by standard microwave characterization in the frequency range of 2–18 GHz. It was found that, for a specific Fe₃O₄@0.125 g RGO composite, the minimum reflection loss can reach −41.89 dB at 6.7 GHz, while the reflection loss was less than −10 dB from 3.4 GHz to 13.6 GHz for a nanocomposite sample thickness in the range of 1–4 mm. The combination of these two materials thus proved to give remarkable microwave absorption properties, owing to enhanced magnetic losses and favorable impedance matching conditions.

Cobalt sulfide composites have exhibited great potential in terms of microwave absorption, owing to their low price, relatively high capacitance, and excellent electrocatalytic activity. Thus, a novel core-shell like structure comprising cobalt sulfide@polypyrrole (CoS@PPy) composite was synthesized by a facile solvothermal synthesis method and in situ polymerization. When coated by the heterostructure polypyrrole aerogel, CoS@PPy composite exhibited excellent microwave absorption properties with an optimal reflection loss (R_L) of −41.8 dB at 6.96 GHz. Furthermore, the absorption bandwidth (R_L < −10 dB) of 5.4 GHz could be reached at a coating thickness of 2.05 mm, probably attributing to the synergistic effect of good impedance matching, interfacial polarization, dipole polarization, and conductivity loss. Moreover, this work proposed a loss mechanism mode which probably occurred in the CoS@PPy composites. It was demonstrated that the CoS@PPy composite is a promising material in the field of electromagnetic wave absorption.

In this study, Fe₃O₄/ZnO core–shell nanocomposites were synthesized through a chemical method of coating the magnetic core (Fe₃O₄) with ZnO by co-precipitation of Fe₃O₄ with zinc acetate in a basic medium of ammonium hydroxide. The phase structure, morphology and electromagnetic parameters of the Fe₃O₄/ZnO core–shell nanocomposites were investigated. The results indicated that the concentration of the solvent was responsible for controlling the morphology of the composites, which further influenced their impedance matching and microwave absorption properties. Moreover, Fe₃O₄/ZnO nanocomposites exhibited an enhanced absorption capacity in comparison with the naked Fe₃O₄ nanospheres. Specifically, the minimum reflection loss value reached −50.79 dB at 4.38 GHz when the thickness was 4.5 mm. It is expected that the Fe₃O₄/ZnO core–shell structured nanocomposites could be a promising candidate as high-performance microwave absorbers.

As a typical two-dimensional material, MXene possesses excellent conductivity and tunable interlayer space, which makes it have an impressive development potential in the field of electromagnetic (EM) waves absorbing materials. In this work, we fabricated a sandwich structure CoS@Ti₃C₂T_x composite using a simple solvothermal process. The CoS nanoparticles are anchored on the Ti₃C₂T_x MXene sheets, forming a heterolayered structure. The results demonstrate that the CoS@Ti₃C₂T_x composites with the sandwich-like architecture showed excellent EM absorbing performance due to the synergistic effects of the conductivity loss, interface polarization, and dipole polarization. When the doping ratio was 40 wt %, the maximum reflection loss value of CoS@Ti₃C₂T_x was up to –59.2 dB at 14.6 GHz, and the corresponding effective absorption bandwidth (below –10 dB) reached 5.0 GHz when the thickness was only 2.0 mm. This work endows a new candidate for the design of MXene-based absorption materials with optimal performance.

To reduce electromagnetic pollution as well as increase the accuracy of high-precision electronic equipment, more attention has been paid to new electromagnetic wave (EMW) absorbing materials, which have the advantages of strong absorption, wide absorption bands, and a narrow thickness. In this study, a novel ternary type of the NiS₂@rGO/polypyrrole (PPy) sandwich-like structured composites was synthesized via a facile two-step method, in which the hydrothermal method was used to prepare NiS₂@rGO binary composites and then the in situ polymerization method was used to synthesize the PPy, which acted as the outer layer of the sandwich-like structure. The morphologies and electromagnetic absorption performance of the NiS₂@rGO/PPy were measured and investigated. A sample with 6 wt% NiS₂@rGO/PPy loading paraffin-composite obtained an outstanding reflection loss (RL) of −58.7 dB at 16.44 GHz under a thickness of 2.03 mm. Simultaneously, the effective electromagnetic wave absorption bandwidth for RL < −10 dB, which covered 7.04 to 18.00 GHz (10.96 GHz), was achieved by changing the thickness of the absorber from 2.0 to 3.5 mm. The results not only suggest that the NiS₂@rGO/PPy composite has excellent performance in the field of EMW absorption but also prove that the novel sandwich-like structure can contribute to appropriate impedance matching through multiple relaxation and interfacial polarization processes.

A novel CoS@Fe₃O₄@rGO aerogel with a unique 3D porous heterostructure was prepared via the solvothermal method, in which cobalt sulfide (CoS) microspheres embedded with Fe₃O₄ nanoparticles were randomly scattered on reduced graphene oxide (rGO) flakes. The introduction of magnetic Fe₃O₄ nanoparticles and rGO regulated the impedance matching, and the excellent electromagnetic wave (EMW) absorption capability of the CoS@Fe₃O₄@rGO aerogel could be attributed to optimal dielectric loss and abundant conductive networks. The results demonstrated that the minimum reflection loss (RL) value of CoS@Fe₃O₄@rGO aerogel was −60.65 dB at a 2.5 mm coating thickness with an ultra-wide bandwidth of 6.36 GHz (10.24–16.6 GHz), as the filler loading was only 6 wt%. Such a lightweight CoS@Fe₃O₄@rGO aerogel with an outstanding absorbing intensity and an ultra-wide effective absorption bandwidth could become a potential EMW absorber.