In this paper, an iterative algorithm for localization of acoustic emission (AE) source is presented. The main advantage of the system is that it is independent of the “ability” in the determination of signal level to triggering the signal by the researcher. The system was tested in cylindrical samples with an AE localized in a known position; the precision in the source determination was of about 2 mm, better than the precision obtained with classic localization algorithms (∼1 cm)

This paper deals with an experimental study of liquid atomization phenomena. For this study an experimental set-up was designed and constructed. A special criterion to start the recording of the process with a high speed digital camera was developed. The frequency dependence of atomization threshold is considered. The theoretical predictions for atomization threshold are also checked. The agreement between the predictions and the experimental results fit qualitatively with the data well until a frequency of 22kHz. For frequencies beyond this value the tendencies are the opposite

The relative dislocation density of aluminum and copper samples is quantitatively measured using linear Resonant Ultrasound Spectroscopy (RUS). For each metallic group, four samples were prepared with different thermomechanical treatments in order to induce changes in their dislocation densities. The RUS results are compared with Nonlinear Resonant Ultrasound Spectroscopy (NRUS) as well as Second Harmonic Generation (SHG) measurements. NRUS has a higher sensitivity by a factor of two to six and SHG by 14–62%. The latter technique is, however, faster and simpler. As a main result, we obtain a quantitative relation between the changes in the nonlinear parameters and the dislocation density variations, which in a first approximation is a linear relation between these differences. We also present a simple theoretical expression that explains the better sensitivity to dislocation content of the nonlinear parameters with respect to the linear ones. X-Ray diffraction measurements, although intrusive and less accurate, support the acoustics results.

The development of titanium foams with a low elastic modulus has increased their scientific and technological relevance due to the evident need to avoid stress shielding problems. In this work, we studied the synthesis and characterization of Ti-13Zr-13Ta-3Nb (wt.%) alloy foams which present high potential for biomedical applications. A Ti-Nb-Ta-Zr mixture was produced by mechanical alloying using a planetary mill. Ti alloy foams were obtained using NaCl as a space-holder (40, 50, and 60 v/v %) that was mixed with the metallic powders and compacted under 420 MPa stress. NaCl particles were removed from the green compacts by submerging samples in distilled water at 60 °C. The green compacts were sintered at 1300 °C for 3 h in Ar atmosphere. Powders and foams were characterized by SEM and optical microscopy. The results showed that Ti-based foams with a tailored heterogeneous pore distribution can be obtained using the space holder method. The elastic modulus (E) of foams was estimated and measured between 5 and 25 GPa using theoretical and finite element analysis (FEA) models which are close to the E values measured experimentally. The results showed that foams with 50% and 60% porosity are potential bone replacement materials because their E value is closer to the E value of human bone.