Magnesium oxysulfate (MOS) cement is a typical eco-friendly cementitious material, which presents excellent performances. In this work, a novel multiscale modeling strategy is proposed to simulate the hydration and pore structure of MOS cement system. This work collected and evaluated the Gibbs free energy of formation for main hydrates and equilibrium constant of main reactions in MOS cement system based on a first principle calculation using Material Studio. Followingly, the equilibrium phase compositions of MOS cement system were simulated through PHREEQC to investigate the molar ratio dependence of equilibrium phase compositions. Results showed that large M (MgO/MgSO₄) was beneficial for the formation of 5Mg(OH)₂·MgSO₄·7H₂O (Phase 517) and large H (H₂O/MgSO₄) tended to decompose MOS cement paste and cause leaching. The microstructure-based method visualized the hydration status of MOS cement systems at initial and ultimate stages via MATLAB and the results showed that large M was significant to reduce porosity, and similar results for the case of small H. Fractal analysis confirms that fractal dimension of pore structure (D_f) was significantly decreased after the hydration of MOS and was positively correlated to the porosity of the paste. In addition, it can be referred that large M and small H were beneficial for modifying the microstructure of MOS paste by decreasing the value of D_f.

Cement-based materials, including cement and concrete, are the most widely used construction materials in the world. In recent years, the investigation and application of fractal theory in cement-based materials have attracted a large amount of attention worldwide. The microstructures of cement-based materials, such as the pore structures, the mesostructures, such as air voids, and the morphological features of powders, as well as the fracture surfaces and cracks, commonly present extremely complex and irregular characteristics that are difficult to describe in terms of geometry but that can be studied by fractal theory. This paper summarizes the latest progress in the investigation and application of fractal theory in cement-based materials. Firstly, this paper summarizes the principles and classification of the seven fractal dimensions commonly used in cement-based materials. These fractal dimensions have different physical meanings since they are obtained from various testing techniques and fractal models. Then, the testing techniques and fractal models for testing and calculating these fractal dimensions are introduced and analyzed individually, such as the mercury intrusion porosimeter (MIP), nitrogen adsorption/desorption (NAD), and Zhang’s model, Neimark’s model, etc. Finally, the applications of these fractal dimensions in investigating the macroproperties of cement-based materials are summarized and discussed. These properties mainly include the mechanical properties, volumetric stability, durability (e.g., permeability, frost and corrosion resistance), fracture mechanics, as well as the evaluation of the pozzolanic reactivity of the mineral materials and the dispersion state of the powders.

Low-heat Portland (LHP) cement is a kind of high-belite cement, which has the characteristic of low hydration heat. Currently, it is extensively used in the temperature control of mass concrete. Based on the thermodynamic database of OPC-based materials, the thermodynamic software GEM-Selektor (noted as GEMS) is used for simulating the hydration products of the LHP cement paste. Then, according to the GEMS thermodynamic simulation results, MATLAB is used to visualize the initial and ultimate stages of LHP cement pastes; the effects of curing temperature and water to cement (w/c) ratio on hydration products are addressed; and the porosity, fractal dimension, and tortuosity of different pastes are calculated. It is found that an appropriately high curing temperature is important for reducing porosity, especially in the early hydration stage. Hydration time also has a significant impact on the hydration of LHP cement paste; long hydration time may reduce the impact of temperature on hydration products. The w/c ratio is another important consideration regarding the hydration degree and porosity of LHP paste, and under different curing temperatures, hydration times, and w/c ratios, the porosity varies from 5.91–32.91%. The fractal dimension of this work agrees with the previous findings. From tortuosity analysis, it can be concluded that the high curing temperature may cause significant tortuosity, further affecting the effective diffusivity of LHP cement paste. For cement pastes with low w/c ratio, this high curing temperature effect is mainly reflected in the early hydration stage, for ones with high w/c ratio, it is in turn evident under long-term curing.

Concrete-face slabs are the primary anti-permeability structures of the concrete-face rockfill dam (CFRD), and the resistance of face slab concrete to permeability is the key factor affecting the operation and safety of CFRDs. Herein, the influences of five fly ash dosages (namely 10%, 20%, 30%, 40% and 50%) on the permeability property of face slab concretes were investigated. Moreover, the difference in the permeability caused by the fly ash dosage variations is revealed in terms of the pore structure and fractal theory. The results illustrate that: (1) The inclusion of 10–50% fly ash lowered the compressive strength of face slab concretes before 28 days of hydration, whereas it contributed to the 180-day strength increment. (2) The incorporation of 10–50% fly ash raised the average water-seepage height (D_m) and the relative permeability coefficient (K_r) of the face slab concrete by about 14–81% and 30–226% at 28 days, respectively. At 180 days, the addition of fly ash improved the 180-day impermeability by less than 30%. (3) The permeability of face slab concretes is closely correlated with their pore structures and D_s. (4) The optimal fly ash dosage in terms of the long-term impermeability and pore refinement of face slab concretes is around 30%. Nevertheless, face slab concretes containing a high dosage of fly ash must be cured for a relatively long period before they can withstand high water pressure.

The effect of atmospheric pressure on performance of air entraining agent (AEA) and air entraining concrete was studied in Tibet and Hubei, China. The result shows that the reduced atmospheric pressure increased surface tension and lowered foaming property of solution. The AEA with excellent foaming ability and stability is preferred in low atmospheric pressure. The freeze‐thaw deterioration process of hardened pastes is relatively faster under low atmospheric pressure. The effect of air pressure on concrete frost resistance performance is more sensitive than the mechanical property. The bigger pores and poor uniformity of internal pore size distribution led to the deterioration of concrete macroscopic properties. Therefore, the AEA varieties should be preferred, the dosage of AEA should be increased, and pore structure of pastes should be optimized to ensure the durability of concrete frost resistance for construction in low‐pressure areas.