The search of suitable combinations of stem cells, biomaterials and scaffolds manufacturing methods have become a major focus of research for bone engineering. The aim of this study was to test the potential of dental pulp stem cells to attach, proliferate, mineralize and differentiate on 3D printed polycaprolactone (PCL) scaffolds. A 100% pure M_w: 84,500 ± 1000 PCL was selected. 5 × 10 × 5 mm³ parallelepiped scaffolds were designed as a wood-pilled structure composed of 20 layers of 250 μm in height, in a non-alternate order ([0,0,0,90,90,90°]). 3D printing was made at 170 °C. Swine dental pulp stem cells (DPSCs) were extracted from lower lateral incisors of swine and cultivated until the cells reached 80% confluence. The third passage was used for seeding on the scaffolds. Phenotype of cells was determined by flow Cytometry. Live and dead, Alamar blue™, von Kossa and alizarin red staining assays were performed. Scaffolds with 290 + 30 μm strand diameter, 938 ± 80 μm pores in the axial direction and 689 ± 13 μm pores in the lateral direction were manufactured. Together, cell viability tests, von Kossa and Alizarin red staining indicate the ability of the printed scaffolds to support DPSCs attachment, proliferation and enable differentiation followed by mineralization. The selected material-processing technique-cell line (PCL-3D printing-DPSCs) triplet can be though to be used for further modelling and preclinical experiments in bone engineering studies.

In craniofacial tissue regeneration, the current gold standard treatment is autologous bone grafting, however, it presents some disadvantages. Although new alternatives have emerged there is still an urgent demand of biodegradable scaffolds to act as extracellular matrix in the regeneration process. A potentially useful element in bone regeneration is strontium. It is known to promote stimulation of osteoblasts while inhibiting osteoclasts resorption, leading to neoformed bone. The present paper reports the preparation and characterization of strontium (Sr) containing hybrid scaffolds formed by a matrix of ionically cross-linked chitosan and microparticles of poly(ε-caprolactone) (PCL). These scaffolds of relatively facile fabrication were seeded with osteoblast-like cells (MG-63) and human bone marrow mesenchymal stem cells (hBMSCs) for application in craniofacial tissue regeneration. Membrane scaffolds were prepared using chitosan:PCL ratios of 1:2 and 1:1 and 5 wt % Sr salts. Characterization was performed addressing physico-chemical properties, swelling behavior, in vitro biological performance and in vivo biocompatibility. Overall, the composition, microstructure and swelling degree (≈245%) of scaffolds combine with the adequate dimensional stability, lack of toxicity, osteogenic activity in MG-63 cells and hBMSCs, along with the in vivo biocompatibility in rats allow considering this system as a promising biomaterial for the treatment of craniofacial tissue regeneration.

Chronic wounds constitute a major clinical and socioeconomic burden owing to prolonged inflammation, persistent bacterial infection, impaired angiogenesis, and defective extracellular matrix remodeling. Advanced wound dressings have traditionally been developed to promote tissue regeneration, control bacterial infection, and restore the wound microenvironment. Recent advances have focused on multifunctional biomaterials integrating regenerative, antibacterial, anti-inflammatory, antioxidant, and controlled drug-delivery properties. Within this context, antiviral biointerface engineering has emerged as a promising, although still exploratory, materials-engineering perspective rather than an established function of wound dressings. Hydrogel–metal–organic framework (MOF) hybrid polymer composites have emerged as versatile platforms for multifunctional wound dressings. Hydrogels provide hydrated three-dimensional matrices with tunable porosity, swelling behavior, mechanical compliance, and biocompatibility, whereas MOFs contribute high surface area, adjustable pore architectures, chemically tailorable active sites, and controlled ion release. Their integration generates synergistic systems whose performance is governed by structure–function relationships involving polymer crosslinking density, MOF dispersion, pore hierarchy, interfacial adhesion, swelling dynamics, and surface functionalization. Collectively, these parameters regulate mass transport, mechanical stability, therapeutic delivery, and cytocompatibility while potentially influencing virus–material interactions through engineered biointerfaces. Current evidence indicates that direct experimental demonstrations of antiviral performance in hydrogel–MOF wound dressing systems remain limited. Accordingly, antiviral biointerface functions should be regarded as emerging engineering opportunities requiring further experimental validation before clinical translation. This review critically analyzes the structure–function engineering principles governing hydrogel–MOF hybrid systems and examines how established regenerative functions may be integrated with emerging antiviral biointerface concepts. Unlike previous reviews focused primarily on drug delivery, antibacterial activity, or tissue engineering, this review emphasizes the relationships between polymer architecture, MOF chemistry, interfacial design, and transport phenomena while explicitly distinguishing experimentally supported evidence from prospective mechanistic concepts. Particular attention is given to current limitations, translational challenges, and future directions for the rational design of next-generation multifunctional hydrogel–MOF wound dressings.

Developing scaffolds with all the necessary mechanical and biological characteristics to mimic cancellous bone and enable its regeneration presents significant challenges. In this work, we leveraged the distinct mechanical properties, elasticity, and degradation kinetics of three distinct polymers. To achieve this, a porogen with a customized internal architecture was produced via 3D printing. A solution containing the blend of the three polymers and jarosite powder was subsequently injected into the printed mold. The porogen structure was then leached away, leaving behind a porous scaffold with the desired internal geometry. This technique enables the fabrication of scaffolds with sinusoidal pores of varying sizes, which facilitate cell viability, proliferation, and nutrient transport. The primary objective of this study was to evaluate the synergistic effects of the three-polymer blend, jarosite doping, and a sinusoidal pore morphology on the behavior of human dental pulp mesenchymal stem cells (hDPMSCs). In vitro evaluations demonstrated that the constructed scaffolds are non-toxic, supporting cell viability, migration, and robust proliferation. Furthermore, the bioactive properties of jarosite and its associated ion release actively promote the differentiation of hDPMSCs into osteogenic lineages, demonstrating strong potential for bone tissue engineering applications.

Chronic wounds are complex environments marked by persistent inflammation, oxidative stress, hypoxia, and conditions that favor antimicrobial resistance (AMR). Conventional antibiotics often fail due to bacterial persistence and the physicochemical barriers of the wound milieu. Biofilm-associated extracellular polymeric substances (EPS), efflux pump activity, quorum sensing (QS), and horizontal gene transfer (HGT) collectively drive antimicrobial tolerance and resistance dissemination, turning chronic wounds into reservoirs of multidrug-resistant pathogens. Consequently, emerging wound therapies demand multifunctional strategies that modulate the wound microenvironment while interfering with resistance-associated phenotypes. Hydrogel–metal–organic framework (MOF) composites have been explored as multifunctional interfaces that combine extracellular matrix-mimetic properties, tunable porosity, stimuli-responsiveness, and controlled therapeutic delivery with the bioactive functions of MOFs. Depending on their composition and architecture, these systems may exert antimicrobial and antibiofilm effects through ionic, electrostatic, osmotic, catalytic, and oxidative mechanisms, while also influencing ROS levels, inflammation, angiogenesis, and local drug transport. However, antimicrobial activity alone does not equate to resistance modulation. Evidence for direct effects on efflux systems, resistance phenotypes, or HGT remains inconsistent across reported platforms. This review critically examines representative hydrogel–MOF systems for chronic wound applications, comparing their composition, physicochemical properties, biological functions, proposed resistance-related mechanisms, advantages, limitations, and current level of evidence. We emphasize distinguishing experimentally demonstrated resistance-modulating effects from mechanistically proposed functions, and identifying design trade-offs and evidence gaps that must be addressed to develop wound interfaces capable of both supporting tissue regeneration and improving infection control.