Adding fibers to concrete helps enhance its tensile strength and ductility. Synthetic fibres are preferable to steel ones which suffer from corrosion that reduces their functionality with time. More consideration is given to synthetic fibres as they can be sourced from waste plastics and their incorporation in concrete is considered a new recycling pathway. Thus, this work investigates the potential engineering benefits of a pioneering application using extruded macro polyfibres in concrete. Two different fiber dosages, 4 kg/m³ and 6 kg/m³, were used to investigate their influence based on several physical, mechanical and microstructural tests, including workability, compressive strength, modulus of elasticity, splitting-tensile strength, flexural test, CMOD, pull-out test and porosity. The test results revealed a slight decrease in the workability of the fibre-reinforced concrete, while all the mechanical and microstructural properties were enhanced significantly. It was observed that the compressive, splitting tensile and bonding strength of the concrete with 6 kg/m³ fibre dosage increased by 19.4%, 41.9% and 17.8% compared to the plain concrete specimens, respectively. Although there was no impact of the fibres on the modulus of rupture, they significantly increased the toughness, resulting in a progressive type of failure instead of the sudden and brittle type. Moreover, the macroporosity was reduced by the fibre addition, thus increasing the concrete compressive strength. Finally, simplified empirical formulas were developed to predict the mechanical properties of the concrete with fibre addition. The outcome of this study will help to increase the implementation of the recycled plastic waste in concrete mix design and promote a circular economy in the waste industry.

Interest in the use of natural fibres as an alternative for artificial fibres in polymer composite manufacturing is increasing for various engineering applications. Their suitability for use in outdoor environments should be demonstrated due to their perceived hydrophilic behaviour. This study investigated the water absorption behaviour of hybrid flax fibre-reinforced epoxy composites with 0%, 0.5%, 1% and 1.5% graphene by weight that were immersed in water for 1000, 2000, and 3000 h. The flexural and interlaminar shear strength before and after immersion in water was then evaluated. The results showed that graphene nanoparticles improved the mechanical properties of the composites. The moisture absorption process of hybrid natural fibre composites followed the Fickian law, whereas the addition of graphene significantly reduced the moisture absorption and moisture diffusion, especially for hybrid composites with 1.5% graphene. However, the flexural and ILSS properties of the composites with and without graphene decreased with the increase in the exposure duration. The flexural strength of hybrid composites with 0%, 0.5%, 1% and 1.5% graphene decreased by 32%, 11%, 17.5% and 13.4%, respectively, after exposure for 3000 h. For inter-laminar shear strength at the same conditioning of 3000 h, hybrid composites with 0.5%, 1% and 1.5% graphene also decreased by 13.2%, 21% and 17.5%, respectively, compared to the dry composite’s strength. The specimens with 0.5% graphene showed the lowest reduction in strength for both the flexural and interlaminar tests, due to good filler dispersion in the matrix, but all of them were still higher than that of flax fibre composites. Scanning electron microscope observations showed a reduction in voids in the composite matrix after the introduction of graphene, resulting in reduced moisture absorption and moisture diffusion.

Fiber-reinforced composites (FRCs) have emerged as transformative alternatives to traditional marine construction materials, owing to their superior corrosion resistance, design flexibility, and strength-to-weight ratio. This review comprehensively examines the current state of FRC technologies in marine deck and underwater applications, with a focus on manufacturing methods, durability challenges, and future innovations. Thermoset polymer composites, particularly those with epoxy and vinyl ester matrices, continue to dominate marine applications due to their mechanical robustness and processing maturity. In contrast, thermoplastic composites such as Polyether Ether Ketone (PEEK) and Polyether Ketone Ketone (PEKK) offer advantages in recyclability and hydrothermal performance but are hindered by higher processing costs. The review evaluates the performance of various fiber types, including glass, carbon, basalt, and aramid, highlighting the trade-offs between cost, mechanical properties, and environmental resistance. Manufacturing processes such as vacuum-assisted resin transfer molding (VARTM) and automated fiber placement (AFP) enable efficient production but face limitations in scalability and in-field repair. Key durability concerns include seawater-induced degradation, moisture absorption, interfacial debonding, galvanic corrosion in FRP–metal hybrids, and biofouling. The paper also explores emerging strategies such as self-healing polymers, nano-enhanced coatings, and hybrid fiber architectures that aim to improve long-term reliability. Finally, it outlines future research directions, including the development of smart composites with embedded structural health monitoring (SHM), bio-based resin systems, and standardized certification protocols to support broader industry adoption. This review aims to guide ongoing research and development efforts toward more sustainable, high-performance marine composite systems.