Ionogels combining ionic liquids with polymer networks show promise for flexible electronics, but their mechanical and functional performance often needs enhancement. Here, we report a series of magnetic nanocomposite ionogels fabricated by doping triiron tetraoxid (Fe₃O₄) nanoparticles into a [C₂mim]⁺[EtSO₄]⁻-dispersed cross-linked PAA matrix. The effect of PAA content (10–20 wt%) on the optical, mechanical, and dielectric properties of pure imidazolium ionogels was first investigated. Increasing PAA concentration enhanced tensile strength (up to ~0.7 MPa) and compressive modulus (~0.65 MPa) while reducing optical transmittance; dielectric relaxation peaks around 6–8 GHz were observed, with the 15 wt% sample showing the highest permittivity. Subsequently, Fe₃O₄ nanoparticles (0–20 wt%) were incorporated into the 10 wt% PAA ionogel. The resulting magnetic ionogels exhibited reduced tensile strength, but significantly increased elongation (up to ~12 strain), indicating network softening. Magnetic hysteresis measurements confirmed superparamagnetic behavior with saturation magnetization reaching ~2.5 emu/g at 20 wt% Fe₃O₄ loading. This work demonstrates a facile strategy to simultaneously tune mechanical, dielectric, and magnetic properties in imidazolium ionogels, providing guidelines for designing soft multifunctional materials for microwave absorption, magnetic actuation, and flexible sensor applications.