Paper is an excellent candidate to replace plastics as a substrate for flexible electronics due to its low cost, renewability and flexibility. Cellulose nanopaper (CNP), a new type of paper made of nanosized cellulose fibers, is a promising substrate material for transparent and flexible electrodes due to its potentially high transparency and high mechanical strength. Although CNP substrates can achieve high transparency, they are still characterized by high diffuse transmittance and small direct transmittance, resulting in high optical haze of the substrates. In this study, we proposed a simple methodology for large-scale production of high-transparency, low-haze CNP comprising both long cellulose nanofibrils (CNFs) and short cellulose nanocrystals (CNCs). By varying the CNC/CNF ratio in the hybrid CNP, we could tailor its total transmittance, direct transmittance and diffuse transmittance. By increasing the CNC content, the optical haze of the hybrid CNP could be decreased and its transparency could be increased. The direct transmittance and optical haze of the CNP were 75.1% and 10.0%, respectively, greatly improved from the values of previously reported CNP (31.1% and 62.0%, respectively). Transparent, flexible electrodes were fabricated by coating the hybrid CNP with silver nanowires (AgNWs). The electrodes showed a low sheet resistance (minimum 1.2 Ω sq⁻¹) and a high total transmittance (maximum of 82.5%). The electrodes were used to make a light emitting diode (LED) assembly to demonstrate their potential use in flexible displays.

Two types of graphene nanoplatelets (xGn and N02) were added to ppoly(lactic acid) (PLA) through solvent mixing to prepare PLA nanocomposites with the aim of producing electrically and thermally conductive PLA products suitable for advanced applications. Transmission electron microscopy (TEM) and X-ray diffraction (XRD) showed that N02 was fully exfoliated and homogenously dispersed in the PLA matrix, while xGn was poorly dispersed with stacked multi-layer structures. Rheological tests were used to characterize the viscoelastic behavior of the nanocomposites and several models/scaling relations based on the rheological results were employed to determine the structure and properties of the percolated graphene networks. The electrical conductivity of the nanocomposites increased by more than twelve orders of magnitude after the graphene concentration reached the percolation threshold. The threshold values obtained from different models showed reasonable agreement.

Styrene-butadiene rubber (SBR) is widely used in the tire, footwear, and belt industries. SBR products contain a high content of carbon black, which is hazardous to human health and the environment. The goal of this study is to investigate the potential of using bio-based cellulose nanofibrils (CNFs) as a replacement for carbon black under simulated industrial formula/processing conditions. CNFs were surface-modified using five different reagents to have either −SH or −C═C functional groups grafted onto their surfaces. Vulcanized SBR sheets reinforced with pristine CNFs, and the five functionalized CNFs were prepared and their properties were tested and compared with those of industrial SBR containing carbon black. All the CNFs, pristine or modified, demonstrated higher reinforcing efficiencies (property increase/amount of reinforcement) than carbon black. The modified CNFs showed even higher reinforcing efficiencies than the pristine ones because of the former’s better dispersion and stronger interfacial bonding. The −SH and −C═C functional groups reduced the hydrophilicity of CNFs and allowed chemical linkages between CNFs and SBR to be established during vulcanization. Solvent (toluene) resistance of the rubber was also improved after the incorporation of CNFs because of the barrier effect of the nanofibers and the restrained SBR chain mobility. The latter also led to reduced rubber damping. Although CNFs provide much stronger reinforcement than carbon black, going forward, SBR/CNFs/carbon black hybrid nanocomposites can also be developed to offer tailorable property combinations that meet different application requirements.