The capillary absorption capacity exerts an important effect on the durability of cement-based materials and is closely related to the pore structure. In this study, a variety of cement-based specimens were examined. The capillary water absorption and pore structure of the samples were determined using a gravimetric method and mercury intrusion porosimetry (MIP), respectively. The capillary water absorption coefficients for different water–binder ratios, diverse types and dosages of mineral admixtures, and various preloads were measured. The experimental results were analyzed and compared with data available in the current literature. The test results showed that the capillary water absorption performance of cement-based materials increased with an increasing water–binder ratio, first decreased and then increased with an increasing fly ash dosage, decreased with an increasing mineral power dosage, and decreased when the preload was less than a critical value and increased rapidly when the preload was greater than the critical value. The relationship between the capillary absorption coefficient and porosity was nearly linear. Water absorption by cement-based materials mainly correlated with pore diameters in the range of 10~1000 nm. The capillary water absorption coefficient increased continuously with the increase of pore fractal dimension.

Cement-based materials with a low water/binder ratio contain a high number of unhydrated cement particles, which implies that a rehydration reaction occurs when they encounter water again. This study aimed to explore how rehydration influences the macroscopic and microscopic properties of cement-based materials. The key study findings included that rehydration could still occur in cement-based materials after one year of hydration, and that the capacity for rehydration-induced repair or damage to cement-based materials depended on whether their internal pores could accommodate rehydration products. During rehydration, the compressive strength and porosity of the specimens were found to first increase and then decrease. The capillary water absorption coefficient decreased continuously over a rehydration period of 120 days. As the water/binder ratio rose, the rehydration rate first increased and then decreased. First, the influence of temperature on the rehydration rate was more noticeable when the water/binder ratio was below 0.3; second, whereas adding large amounts of fly ash and silica fume did not prove to be conducive to repairing and enhancing cement-based materials undergoing rehydration, adding slag and small quantities of silica fume, or alternatively compounding small amounts of silica fume and fly ash could improve the repair and enhancement effects of rehydration.