Blue-luminescent N-doped carbon quantum dots (NCQDs) exhibiting rarely observed excitation independent optical properties are synthesised from citric acid in the presence of ammonia via a Continuous Hydrothermal Flow Synthesis (CHFS) approach. CHFS is an eco-friendly, rapid synthetic approach (within fractions of a second) facilitating ease of scale-up industrialization as well as offering materials with superior properties. The synthesised NCQDs readily disperse in aqueous solution, have an average particle size of 3.3 ± 0.7 nm, with highest emission intensity at 441 nm (and a narrow full width at half maximum, FWHM ∼78 nm) under a 360 nm excitation wavelength. N-doped carbon quantum dots, without any further modification, exhibited a high selectivity and sensitivity as a nano-sensor for the highly toxic and carcinogenic chromium(VI) ions. The nano-chemo-sensor delivers significant advantages including simplicity of manufacturing via a continuous, cleaner technology (using targeted biomass precursor), high selectivity, sensitivity and fast response leading to potential applications in environmental industry as well photovoltaics, bio-tagging, bio-sensing and beyond.

Green fluorescent graphene quantum dots (GQD) have been synthesized via hydrothermal fragmentation using a continuous hydrothermal flow synthesis (CHFS) process as a single, rapid and environmentally benign method. This is in the presence of p-phosphonic acid calix[4]arene which enhances the optical properties of the graphene quantum dots through surface functionalization, with photoluminescence quantum yields of up to 4.5%. Potential environmental impact of a lab-scale supercritical CHFS process compared with that of conventional batch processing of GQDs has been assessed using the method of the International Reference Life Cycle Data System (ILCD).

A rapid synthesis of TiO₂ hybrids with significant enhancement in photocatalytic activity is reported. Using state-of-the-art techniques including sophisticated DFT calculations, we report insight into the charge transfer and modulation of the energy band edges.

MXene (Ti ₂ CT _x ) is exfoliated in a vortex fluidic device (VFD), as a thin film microfluidic platform, under continuous flow conditions, down to ca 3 nm thin multi-layered two-dimensional (2D) material, as determined using AFM. The optimized process, under an inert atmosphere of nitrogen to avoid oxidation of the material, was established by systematically exploring the operating parameters of the VFD, along with the concentration of the dispersed starting material and the choice of solvent, which was a 1 : 1 mixture of isopropyl alcohol and water. There is also some fragmentation of the 2D material into nanoparticles ca 68 nm in diameter.