The size effects in metal forming have been found to be crucial in micro-scale plastic deformation or micro-forming processes, which lead to attenuation of the material’s formability due to the increasing heterogeneity of the plastic flow. The use of an electric field during micro-scale plastic deformation has shown to relieve size effects, enhance the material’s formability, modify the microstructure, etc. Consequently, these electric-assisted (EA) micro-forming processes seem to bring many potential benefits that need to be investigated. Accordingly, here we investigated the influence of an electric field on the size effects to describe the fracture behavior in uniaxial micro-tension tests of an AZ31 alloy with various grain sizes. In order to decouple the thermal-mechanical and microstructure changes, room temperature (RT), oven-heated (OH), air-cooled (AC), and EA uniaxial micro-tension tests were conducted. The size effects contribution on the fracture stress and strain showed a similar trend in all the testing configurations. However, the smallest fracture stresses and the largest fracture strains were denoted in the EA configuration. EBSD examination shows that current-induced dynamic recrystallization (DRX) and texture evolution could be negligible under the studied conditions. The kernel average misorientation (KAM) maps give the larger plastic deformation in the EA specimens due to the reduction of plastic micro-heterogeneity. Finally, the fracture morphology indicates that the current-induced ductility enhancement may be attributed to the arrest of micro-crack propagation and the inhibition of void initiation, growth, and coalescence caused by lattice melting and expansion.

Texture surface containing both micro-pits and a thin carbon coating was produced using laser surface texturing and magnetic-control vacuum sputtering. Tribological properties of the laser-textured surface coated with thin carbon were experimentally investigated at low-temperature (8–10 °C) under starved and lubricated conditions with a ring-on-ring test rig. The results indicated that the laser-textured surface combined with carbon coating (textured + coating) exhibited low wear intensity and friction coefficient under lubricated conditions, while moderate wear was observed under starved lubrication conditions as compared with the smooth, textured, and carbon-coated surfaces. The wear mechanisms of the lubricated, textured, coated surface under three working conditions (10 N and 1.25 m/s, 16 N and 0.25 m/s, and 50 N and 0.05 m/s) revealed plowing effect, corrosion, and adhesive wear, while oxidative and adhesive wears were observed under starved lubrication. Finally, the textured, coated surface was freely adaptable to different working conditions and exhibited additional effects for better tribological applications at low-temperature as compared with the smooth, laser-textured, and carbon-coated surfaces.

Ultrasonic vibration (UV) is widely used in the forming, joining, machining process, etc. for the acoustic softening effect. For parts with small dimensions, UV with limited output energy is very suitable for the microforming process and has been gaininf more and more attention. In this investigation, UV-assisted uniaxial tensile experiments were carried out utilizing GB 5052 thin sheets of different thicknesses and grain sizes, respectively. The coupling effects of UV and the specimen dimension on the properties of the material were analyzed from the viewpoint of acoustic energy in activating dislocations. A reduction of flow stress was found for the existing acoustic softening effects of UV. Additionally, the residual effects of UV were demonstrated when UV was turned off. The uniform deformation ability of thin sheet could be improved by increasing the hardening exponent with UV. The experimental results indicate that UV is very helpful in improving the forming limit in microsheet forming, e.g., microbulging and deep drawing processes.

Developing bio-inspired functional surfaces on engineering metals is of extreme importance, involving different industrial sectors, like automotive or aeronautics. In particular, micro-embossing is one of the efficient and large-scale processes for manufacturing bio-inspired textures on metallic surfaces. However, this process faces some problems, such as filling defects and die breakage due to size effect, which restrict this technology for some components. Electrically assisted micro-forming has demonstrated the ability of reducing size effects, improving formability and decreasing flow stress, making it a promising hybrid process to control the filling quality of micro-scale features. This research focuses on the use of different current densities to perform embossed micro-channels of 7 μm and sharklet patterns of 10 μm in textured bulk metallic glass dies. These dies are prepared by thermoplastic forming based on the compression of photolithographic silicon molds. The results show that large areas of bio-inspired textures could be fabricated on magnesium alloy when current densities higher than 6 A/mm² (threshold) are used. The optimal surface quality scenario is obtained for a current density of 13 A/mm². Additionally, filling depth and depth–width ratio nonlinearly increases when higher current densities are used, where the temperature is a key parameter to control, keeping it below the temperature of the glass transition to avoid melting or an early breakage of the die.

SiBZrOC quinary ceramics were obtained through the modification of a SiOC precursor with B(OH)₃and Zr(OnPr)₄.

Bent micro-tubes have been frequently applied in electronics, medical devices and aerospace for heat transfer due to the increasing heat flux in high-density electric packages. Rotary-draw bending (RDB) is a commonly used process in forming tubes due to its versatility. However, the control of forming defects is the key problem in micro-tube bending in terms of wall thinning, cross-sectional deformation and wrinkling. In this paper, a three-dimensional (3D) finite-elements (FE) modeling of electrically-assisted (EA) RDB of 6063 aluminum alloy micro-tubes is developed with the implicit method in ABAQUS. The multi-field coupled behavior was simulated and analyzed during the EA RDB of micro-tubes. Several process parameters such as micro-tube diameter, bending radius, current density and electrical load path were selected to study their effects on the bending defects of the Al6063 micro-tubes. The simulated results showed that the cross-sectional distortion could be improved when electrical current mainly pass through the vicinity of the tangent point in the micro-tube RDB, and the cross-sectional distortion tended to decrease with the increases of current density and tube diameter, and the decreases of bending speed and radius. A trade-off should be made between the benefit and side effect due to electrical current since the risk of wall thinning and wrinkling may increase.