This article describes the production of nanoparticles of Chilean natural zeolite, using three size reduction methods: Ball mill, microgrinding, and microfluidization. Morphological characterization of samples indicated an average diameter of 37.2 ± 15.8 nm of the zeolite particles. The size reduction and chemical treatments did not affect the morphology or integrity of the zeolite. An increase of the zeolite samples’ Si/Al ratio was observed after the acid treatment and was confirmed by SEM-EDX analysis. Moreover, the effectiveness of the copper salt ion exchange (Cu²⁺) to the zeolite nanoparticles was analyzed by SEM-EDX. XRD analysis indicated that clinoptilolite and mordenite are the main phases of Chilean natural zeolite, and the crystalline structure was not affected by the modification processes. The FTIR characterization showed the presence of chemical bonds of copper with the zeolite nanoparticle framework. The ion-exchanged zeolite nanoparticles were evaluated for antibacterial behavior by the disc diffusion method. Additionally, the minimum inhibitory concentration and minimum bactericidal concentration were obtained. Microbiological assays with copper-exchanged nanozeolites showed an antimicrobial activity with a bactericidal effect against Escherichia coli and Staphylococcus aureus, which are the primary pathogens of food and are also resistant to multiple drugs. In this study, a new application for natural nanozeolites is demonstrated, as the incorporated copper ions (Cu²⁺) in nanozeolites registered a productive antibacterial activity.

Nanocellulose (NC) is a promising material for drug delivery due to its high surface area-to-volume ratio, biocompatibility, biodegradability, and versatility in various formats (nanoparticles, hydrogels, microspheres, membranes, and films). In this study, nanocellulose films were derived from “Bolaina blanca” (Guazuma crinita) and combined with nanoporous silicon microparticles (nPSi) in concentrations ranging from 0.1% to 1.0% (w/v), using polyvinyl alcohol (PVA) as a binding agent to create NC/nPSi composite films for drug delivery systems. The physicochemical properties of the samples were characterized using UV-Vis spectroscopy, scanning electron microscopy (SEM), Fourier transform infrared spectroscopy–attenuated total reflectance (FTIR–ATR), X-ray diffraction (XRD), and thermogravimetric analysis (TGA). The mechanical properties and drug release capabilities were also evaluated using methylene blue (MB) as an antibacterial drug model. Antibacterial assays were conducted against S. aureus and E. coli bacteria. The results show that NC/nPSi composites with 1% nPSi increased the T_50% by 10 °C and enhanced mechanical properties, such as a 70% increase in the elastic modulus and a 372% increase in elongation, compared to NC films. Additionally, MB released from NC/nPSi composites effectively inhibited the growth of both bacteria. It was also observed that the diffusion coefficients were inversely proportional to the % nPSi. These findings suggest that this novel NC/nPSi-based material can serve as an effective controlled drug release system.

Quasistatic nanoindentation is a proven tool that provides information on the micromechanical behavior of wood cell walls. However, quasistatic tests cannot probe the time-dependent mechanical behavior shown by wood. Nanoindentation dynamic mechanical analysis (nanoDMA) can measure the viscoelastic properties of wood cell walls. This research aimed to study the quasistatic and viscoelastic properties of individual radiata pine wood (Pinus radiata D. Don) cell wall layers. To minimize variability and retrieve both properties at the same locations, a load function composed of a multiload-quasistatic function followed by dynamic reference frequency segments was developed. Nanoindentations were then performed on the S2 layer and compound corner middle lamella (CCML) of unembedded latewood cells. Because the S2 layer is anisotropic, both transverse and longitudinal–tangential wood planes were studied. In the transverse plane, the average results of the quasistatic elastic moduli $\left(E_s\right)$ for the S2 layer and CCML were 15.7 GPa and 4.6 GPa, respectively. In the longitudinal–tangential plane, the $E_s$ was 3.9 GPa. In the transverse section, the hardness $\left(H\right)$ of the S2 layer and CCML were 331 MPa and 277 MPa, respectively, and in the longitudinal–tangential section H was 244 MPa. To acquire the viscoelastic properties, measurements were made over more than three decades of frequency. An increase of the storage modulus $\left(E^{\prime }\right),$ and a reduction of the loss modulus $\left(E^{″}\right)$ and loss factor $\left(\tan \delta \right)$ as frequency increased were found in both wood orientations. The quasi-static and dynamic indentations equivalent at 0.1 Hz showed similar values for $E_s$ and E′. This study contributes to our knowledge of wood cell wall micromechanical properties.

This research evaluated the contribution of nanocomposite films based on different concentrations of nZH-Cu (1%, 2%, and 3%) to the microbiological, organoleptic, and physicochemical characteristics of packed chicken breast meat. Analysis of some meat quality traits, such as microbiological, chemical, and physical, were conducted on a laboratory scale. For this, small squares of chicken breast meat, weighing approximately 10 g, were aseptically wrapped with rectangular pieces of 5 × 10 cm PLA-nZH-Cu nanocomposite films, which were stored at 4 °C for 20 days. The microbiological results indicated efficient antibacterial activity (at any nZH-Cu concentration in the nanocomposite films) on the total viable count of groups of psychrophiles, aerobic mesophiles, Enterobacteriaceae, and Salmonella spp. until day 10 of storage (p < 0.05). No significant changes were observed in the organoleptic (color) and physicochemical qualities (texture, weight, pH, and acidity) until day 10 of storage at 4 °C (p < 0.05). The analysis of the experimental tests carried out determined that the PLA-nZH-Cu nanocomposite films played an effective role in the bacterial safety of the packaged chicken. It was concluded that the nZH-Cu nanocomposite films, at all concentrations tested, extended the shelf life of the chicken breast meat for up to 10 days in a refrigerator at 4 °C.

The main objective of this study was to develop cellulose nanofibers from the thermomechanical pulp (TMP) of Radiata Pine (Pinus radiata D. Don), and for this, a one-step micro-grinding process was used. The newly developed material was called thermomechanical pulp nanofibers (TMP-NF). In the first instance, a determination of the constituents of the TMP was carried out through a chemical characterization. Then, TMP-NFs were compared with cellulose nanofibers (CNF) by morphological analysis (Scanning Electron Microscopy, SEM, and Atomic Force Microscopy, AFM), X-ray Diffraction (XRD) and Fourier-Transform Infrared Spectroscopy with Attenuated Total Reflection (FTIR-ATR). In addition, films were developed from TMP-NF and CNF using a vacuum filtration manufacturing method. For this study, 0.10, 0.25, 0.50, and 1.00% dry weight of CNF and TMP-NF were used as continuous matrices without organic solvents. The films were characterized by determining their morphological, physical, surface properties, and mechanical properties. The main results showed that morphological analysis by SEM and AFM for the fractionated sample indicated a fiber diameter distribution in the range of 990-17 nm and an average length of 5.8 µm. XRD analysis showed a crystallinity index of 90.8% in the CNF, while in the TMP-NF, it was 71.2%, which was foreseeable. FTIR-ATR analysis showed the functional groups of lignin and hemicellulose present in the TMP-NF sample. The films presented apparent porosity values of 33.63 for 1.00% solids content of CNF and 33.27% for 0.25% solids content of TMP-NF. The contact angle was 61.50° for 0.50% solids content of CNF and 84.60° for 1.00% solids content of TMP-NF. Regarding the mechanical properties, the modulus of elasticity was 74.65 MPa for CNF and 36.17 MPa for TMP-NF, and the tensile strength was 1.07 MPa for CNF and 0.69 MPa for TMP-NF. Although the mechanical properties turned out to be higher in the CNF films, the TMP-NF films showed improved surface characteristics as to surface hydrophobic and apparent porosity. In addition, the easy and rapid obtaining of TMP nanofibers makes it a promising material that can be used in biologically based nanocomposites.