The synthesis of copper nanoparticles (Cu NPs) stable to chemical oxidation has attracted much attention due to their novel application possibilities. The physicochemical properties of Cu NPs define their utilization in diverse fields, including biological applications, solar cells, high conductivity inks for printed electronics, and other specific applications. In this study we present the synthesis of oxide-free Cu NPs by wet chemistry routes and their chemical oxidation during the storage exposed to ambient conditions. The Cu NPs synthesized in PAAm and AAm/glycerol presence exhibit no oxidation during synthesis and atmospheric conditions storage for 60 and 37 months, respectively. The obtained results compared with those coming from oxidation of partially passivated commercial Cu NPs at 99.8% purity, are presented. The role of the Cu NPs coating is critical to avoid oxidation, and it can be an important feature to achieve good dispersion in different polymers. The Cu NPs oxidation was studied by XRD, TGA, TEM, FTIR, and HR-TEM.

In this study, the effect of pure and modified hexagonal boron nitride (h-BN) nanosheet incorporation on the stability, viscosity, and electrochemical behavior of a waterborne emulsion acrylic coating was studied. The functionalization of h-BN nanoplatelets with polyacrylic acid (PAA) plasma polymerization was performed, and the successful surface modification was determined through water dispersion testing, Fourier transform infrared spectroscopy and thermogravimetric analysis, X-ray photoelectron spectroscopy, and also by transmission electronic microscopy. Later, the stability and viscosity properties of emulsion nanostructured acrylic coatings, which were previously prepared by an ultrasound-assisted mixing system, were analyzed using zeta potential and rheometry testing, respectively. The electrochemical behavior was analyzed by electrochemical impedance spectroscopy. The results prove an effective deposition of PAA films on the h-BN surfaces, which enhanced the stability and viscosity acrylic of nanostructured coatings due to the interactions between the h-BN nanoplatelets surface and emulsion acrylic paint and also with the thickener additives. On the other hand, the electrochemical analysis demonstrated a significant increase (two orders of magnitude) in corrosion resistance in the acrylic nanostructured coatings with 1 wt.% of unmodified and modified h-BN nanoplatelets concerning pure acrylic paint due to a barrier protection mechanism of corrosion inhibition. Therefore, the results demonstrate that the surface modification of h-BN by plasma polymerization (green technology) helped to solve the low dispersibility issue of BN nanosheet surfaces in a waterborne polymer matrix to obtained green nanostructured acrylic coatings with the right balance in in-can properties and corrosion inhibition of AISI 304 stainless steel.

Isotactic polypropylenes (iPP) with different melt flow indexes (MFI) were used to fabricate nanocomposites (NCs) with 10 wt % loadings of multi-wall carbon nanotubes (MWCNTs) using ultrasound-assisted extrusion methods to determine their effect on the morphology, melt flow, and electrical properties of the NCs. Three different types of iPPs were used with MFIs of 2.5, 34 and 1200 g/10 min. Four different NC fabrication methods based on melt extrusion were used. In the first method melt extrusion fabrication without ultrasound assistance was used. In the second and third methods, an ultrasound probe attached to a hot chamber located at the exit of the die was used to subject the sample to fixed frequency and variable frequency, respectively. The fourth method is similar to the first method, with the difference being that the carbon nanotubes were treated in a fluidized air-bed with an ultrasound probe before being used in the fabrication of the NCs with no ultrasound assistance during extrusion. The samples were characterized by MFI, Optical microscopy (OM), Scanning electron microscopy (SEM), Transmission electron microscopy (TEM), electrical surface resistivity, and electric charge. MFI decreases in all cases with addition of MWCNTs with the largest decrease observed for samples with the highest MFI. The surface resistivity, which ranged from 10¹³ to 10⁵ Ω/sq, and electric charge, were observed to depend on the ultrasound-assisted fabrication method as well as on the melt flow index of the iPP. A relationship between agglomerate size and area ratio with electric charge was found. Several trends in the overall data were identified and are discussed in terms of MFI and the different fabrication methods.

Background: Propagation of pathogens has considered an important health care problem due to their resistance against conventional antibiotics. The recent challenge involves the design of functional alternatives such as nanomaterials, used as antibacterial agents. Early stages of antibacterial damage caused by metallic nanoparticles (NPs) were studied by Transmission Electron Microscopy (TEM) and combined Scanning Transmission Electron Microscopy with High Angle Annular Dark Field (STEM-HAADF), aiming to contribute to the elucidation of the primary antibacterial mechanism of metallic NPs. Methods: We analyze the NPs morphology by TEM and their antibacterial activity (AA) with different amounts of Ag and Cu NPs. Cultured P. aeruginosa were interacted with both NPs and processed by TEM imaging to determine NPs adhesion into bacteria wall. Samples were analyzed by combined STEM-HAADF to determine the NPs penetration into bacterium and elemental mapping were done. Results: Both NPs displays AA depending on NPs concentration. TEM images show NPs adhesion on bacterial cells, which produces morphological changes in the structure of the bacteria. STEMHAADF also proves the NPs adhesion and penetration by intracellular localization, detecting Ag/Cu species analyzed by elemental mapping. Moreover, the relative amount of phosphorus (P) and sulfur (S) increases slightly in P. aeruginosa with the presence of NPs. These elements are associated with damaged proteins of the outer cell membrane. Conclusions: Combined microscopy analyses suggest that the early stages of antibacterial damage caused by alteration of bacterial cell wall, and can be considered a powerful tool aiming to understand the primary antibacterial mechanism of NPs.