Polymer nanocomposites have attracted global attention as a metal replacement for electrical and electronic applications. Graphene nanoplatelets (GNPs) are widely used as a nanoreinforcement to enhance the functional and structural properties of thermoset and thermoplastic polymers. In the present study, ABS nanocomposites were prepared by reinforcing 3–15 wt.% GNPs in steps of 3 wt.%. The neat ABS and ABS+GNP nanocomposite specimens for the mechanical test were prepared using injection molding, followed by extrusion, as per American Society for Testing and Materials (ASTM) standards. It was found that the modulus of ABS improved due to the reinforcement of GNPs. Additionally, we noticed higher thermal stability of nanocomposites due to the faster heat-conducting path developed in the nanocomposites by the presence of GNPs. However, observed agglomeration of GNPs at higher concentrations and poor wetting with ABS led to the deterioration of the mechanical properties of the nanocomposites. Moreover, 350 µm thick nanocomposite films were manufactured by compression molding, followed by the extrusion method, and we investigated their electrical conductivity, magnetic permeability, permittivity, and electromagnetic-wave-shielding effectiveness. The developed nanocomposites showed improved conductivity and effective electromagnetic wave shielding by absorption. The 15 wt.% GNP-reinforced ABS composite film showed a maximum shielding effectiveness of 30 dB in the X-band.

The multi-walled carbon nanotubes (MWCNTs) and the poly(acrylonitrile-co-butadiene-co-styrene) (ABS) granulates are dispersed in acetone separately using a magnetic stirrer followed by ultrasonication. Further, both the solutions were mixed with magnetic stirring followed by ultrasonication. Neat-ABS film, 0.25 wt%, 0.5 wt% and 1 wt% of MWCNT-ABS nanocomposite films of the average thickness of 140 µm are fabricated by the solution molding using a petri dish, followed by room temperature curing and further hot compression to maintain uniform thickness. The tensile properties, thermal stability, electrical conductivity, and EMSE of all films are investigated. The results indicate that the addition of MWCNTs to ABS enhanced the mechanical properties and electrical conductivity, thermal stability, and EMSE. The 0.25 wt% MWCNT-ABS nanocomposite films show attractive mechanical, electrical, thermal, and EMSE as compared to neat-ABS films. More than 0.25 wt% MWCNTs in the ABS matrix deteriorates the tensile strength. However, 0.5 wt% MWCNT-ABS nanocomposites exhibit better tensile strength, Young’s modulus, electrical conductivity, and EMSE than neat-ABS. In this research, we used a low quantity of MWCNTs and followed a one-time heating process in the entire fabrication, and produced MWCNT-ABS nanocomposite films with reasonable properties. Hence, this may be one of the options to produce nanocomposites suitable for EMS materials. We recommend that these films may be used as interlayers to develop an X-band range electromagnetic wave shielding material.

Aging populations and the increase in chronic diseases worldwide demand efficient healthcare tools for simple, rapid, and accurate diagnosis and monitoring the human health. In this context, gas sensors are used to analyze the type of gas in the breath to diagnose chronic diseases. Metal oxide and ceramic nanofibers (NFs) produced by the electrospinning (ES) method have been investigated for potential use as gas sensors in the engineering and medical sectors. The material and process parameters are the main influencing factors on the functional performance of electrospun metal oxide NFs. Zinc oxide (ZnO) based NFs are used in various gas sensors due to the wide band gap (3.37eV), large exciton binding energy, and high mobility of charge carriers of ZnO. In this research, we made an attempt to study the effect of poly(vinyl alcohol) (PVA) and zinc acetate dihydrate (ZnAc₂) concentrations and feed rate, voltage, spinneret tip-to-collector distance (TCD), and pyrolysis temperature on the physical properties of ZnO NFs. An average fiber diameter of 119 nm was obtained after pyrolysis at 600 °C of electrospun fiber produced from an aqueous PVA solution of concentration 15 w% with 7.5 w% ZnAc₂ based on the weight of PVA. The grain size, transmittance, structural defects, and band gap energy of NFs were found to increase as a function of the pyrolysis temperature, which could be beneficial for the functional applications of these NFs.

Metal-coated synthetic fiber reinforced polymer composites have been recently used for many electrical and electronic applications. In this direction, due to low weight, noncorrosive, and excellent structural properties, the carbon fabric reinforced polymer composites are in high demand. In this work, we developed Fe2O3 film on bi-axial oriented plain viewed carbon fabric by spray pyrolysis at various thicknesses using FeCl2.H2O solution. XRD study revealed that the film consisted of α-Fe2O3 and no other crystalline phase was observed. The Fe3+concentration were varied and the samples was characterized for electrical, magnetic properties and morphology study. The coating on the fabric surface was found to be uniform and covered the entire fiber surface when the spray volume was 40 ml. The Fe3+ content on the fabric increased with the increase in the solution concentration. It was noticed that α-Fe2O3 coated on the fabric surface increased the conductivity and magnetic property making this may be suitable for Electromagnetic interference (EMI) shielding applications.

Design and analysis of a stepped impedance elliptical microstrip low pass filter has been described in this paper. To improve the frequency response, fractals have been proposed in the conventional design. Simulated and measured results of the conventional as well as the fractal filter have been analyzed.