The mineralization of tetracycline by electrochemical advanced oxidation processes (EAOPs) as well as the study of the toxicity of its intermediates and degradation products are presented. Electro-Fenton (EF), anodic oxidation (AO), and electro-Fenton coupled with anodic oxidation (EF/AO) were used to degrade tetracycline on carbon felt (cathode) and a sub-stoichiometric titanium oxide (Ti₄O₇) layer deposited on Ti (anode). As compared to EF and AO, the coupled EF/AO system resulted in the highest pollutant removal efficiencies: total organic carbon removal was 69 ± 1% and 68 ± 1%, at 20 ppm and 50 ppm of initial concentration of tetracycline, respectively. The effect of electrolysis current on removal efficiency, mineralization current efficiency, energy consumption, and solution toxicity of tetracycline mineralization were investigated for 20 ppm and 50 ppm tetracycline. The EF/AO process using a Ti₄O₇ anode and CF cathode provides low energy and high removal efficiency of tetracycline caused by the production of hydroxyl radicals both at the surface of the non-active Ti₄O₇ electrode and in solution by the electro-Fenton process at the cathodic carbon felt. Complete removal of tetracycline was observed from HPLC data after 30 min at optimized conditions of 120 mA and 210 mA for 20 ppm and 50 ppm tetracycline concentrations. Degradation products were elucidated, and the toxicity of the products were measured with luminescence using Microtox^® bacteria toxicity test.

Cellulose nanocrystals (CNCs) are bio-based materials able to be functionalized following different approaches, which expands their range of applications. One such approach is surface-initiated polymerization, which involves the attachment of an initiator to the CNC’s surface to initiate the growth of the polymer. This work reports the modification of CNCs using the described approach. First, a CNC-based film was prepared, on which an initiator (RAFT agent) was grafted, and then (trimethylaminoethyl methacrylate, a positively charged monomer, was polymerized using reversible addition–fragmentation chain-transfer (RAFT) polymerization. The CNC film was successfully modified and fully characterized. Different degrees of polymerization were targeted to emphasize the effect of the positively charged polymer and their chain length on the adsorption efficiency. The results showed that by increasing the chain length of the grafted polymer, up to 80% of both pollutants could be removed, with a faster adsorption of PFOS as compared to PFOA.