By combining results of adsorption/desorption measurements on powders and electrical conductivity studies on thick and thin films, the interaction of indium tin oxide with various ambient gas species and carbon monoxide as potential target gas was studied between room temperature and 700 °C. The results show that the indium tin oxide surfaces exhibit a significant coverage of water-related and carbonaceous adsorbates even at temperatures as high as 600 °C. Specifically carbonaceous species, which are also produced under carbon monoxide exposure, show a detrimental effect on oxygen adsorption and may impair the film’s sensitivity to a variety of target gases if the material is used in gas sensing applications. Consequently, the operating temperature of an ITO based chemoresistive carbon monoxide sensor should be selected within a range where the decomposition and desorption of these species proceeds rapidly, while the surface oxygen coverage is still high enough to provide ample species for target gas interaction.

A zirconia-based potentiometric solid electrolyte gas sensor with internal solid state reference was used to study the response behavior of platinum cermet and indium tin oxide sensing electrodes. Target gases included both oxygen and carbon monoxide in nitrogen-based sample gas mixtures. It was found that with the indium tin oxide sensing electrode, the low-temperature behavior is mainly a result of incomplete equilibration due to contaminations of the electrode surface. On the other hand, some of these contaminant species have been identified as being pivotal for the higher carbon monoxide sensitivity of the indium tin oxide sensing electrode as compared to platinum cermet electrodes.

The electrode processes governing response behavior of a solid electrolyte CO₂ sensor have been studied using electrochemical impedance spectroscopy on symmetric cells exposed to various temperatures and gas compositions. It was shown that the electrochemical processes leading to potential formation at the Au/Na₂CO₃ electrode can be described by adapting models commonly used in the field of molten carbonate fuel cells.

The influence of various gas compositions on surface adsorbate species and electrical conductivity of indium tin oxide (ITO) powders and thick films was studied. By combining results of temperature dependent desorption (TPD) with electrical conductivity measurements it was shown that, after exposure to ambient air, the surfaces of both powders and films are covered with significant amounts of oxygen, water and carbon related species. While the influence of oxygen adsorbates has already been described for temperatures below 500 °C, desorption of some of these species could be detected at temperatures as high as 675 °C, with a significant influence on electrical film conductivity.