A study to produce cellulose nanofibrils (CNF) from kraft cellulose pulp was conducted using a centroid simplex mixture design. The enzyme blend contains 69% endoglucanase and 31% exoglucanase. The central composite rotational design (CCRD) optimized the CNF production process by achieving a higher crystallinity index. It thus corresponded to a solid loading of 15 g/L and an enzyme loading of 0.974. Using the Segal formula, the crystallinity index (CrI) of the CNF was determined by X-ray diffraction to be 80.87%. The average diameter of the CNF prepared by enzymatic hydrolysis was 550–600 nm, while the one produced by enzymatic hydrolysis and with ultrasonic dispersion was 250–300 nm. Finally, synergistic interactions between the enzymes involved in nanocellulose production were demonstrated, with Colby factor values greater than one.

Biosensors based on nanomaterial composites have been investigated for their potential to function as high sensitivity signal response devices. In the present study, we report the fabrication of silver nanoparticles (AgNPs) on a graphite epoxy composite electrode (GEC) and mixed with the polyaniline (a conductive emeraldine salt form polymer) composite electrode (AgNPs/PANI/GEC), in order to compare the performance of the generated electrochemical response signals. Cyclic voltammetry tests were conducted to compare the quality and intensity of signals from the different prepared electrodes. Tests for the AgNPs/PANI/GEC electrodes were made with and without the enzymes alcohol oxidase and horseradish peroxidase immobilized on the composite surface. The prepared AgNPs/PANI/GEC nanocomposite was evaluated by thermal analysis. Scanning electron microscopy images and EDX were obtained for characterization of the electrode surface morphology. Square wave voltammetry techniques were then employed for ethanol analysis with the AOX/HRP/AgNPs/PANI/GEC biosensor achieving good results in a range of 0.37M to 0.65 M.