Arsenic (As)-laden wastewater may pose a threat to biodiversity when released into soil and water bodies without treatment. The current study investigated the sorption properties of both As(III, V) oxyanions onto iron hydroxide (FHO) by chemical coagulation. The potential mechanisms were identified using the adsorption models, ζ-potential, X-ray diffraction (XRD) and Fourier Transform Infrared Spectrometry (FT-IR) analysis. The results indicate that the sorption kinetics of pentavalent and trivalent As species closely followed the pseudo-second-order model, and the adsorption rates of both toxicants were remarkably governed by pH as well as the quantity of FHO in suspension. Notably, the FHO formation was directly related to the amount of ferric chloride (FC) coagulant added in the solution. The sorption isotherm results show a better maximum sorption capacity for pentavalent As ions than trivalent species, with the same amount of FHO in the suspensions. The thermodynamic study suggests that the sorption process was spontaneously exothermic with increased randomness. The ζ-potential, FT-IR and XRD analyses confirm that a strong Fe-O bond with As(V) and the closeness of the surface potential of the bonded complex to the point of zero charge (pH_zpc) resulted in the higher adsorption affinity of pentavalent As species than trivalent ions in most aquatic conditions. Moreover, the presence of sulfates, phosphates, and humic and salicylic acid significantly affected the As(III, V) sorption performance by altering the surface properties of Fe precipitates. The combined effect of charge neutralization, complexation, oxidation and multilayer chemisorption was identified as a major removal mechanism. These findings may provide some understanding regarding the fate, transport and adsorption properties onto FHO of As oxyanions in a complex water environment.

The purpose of this study is to control the viscous behavior of lightweight aggregates through the chemical design of a lightweight aggregates material in order to solve the problem of the adhesion of lightweight aggregates by viscous behavior in the bloating activation temperature range of lightweight aggregates. In order to induce a reduction of Fe₂O₃ inside the aggregates, Fe₂O₃ and carbon were added to acid clay so as to produce aggregate. The particle density and the water absorption rate of the aggregates were measured, the cross-section was observed with an optical microscope, and the distribution of hematite of the lightweight aggregates was confirmed by a 3D CT analysis. Pilot scale rotary kiln experiments were performed. The optimal additive contents for the production of lightweight aggregates using acid clay were 8–13 wt% of Fe₂O₃ and 2–3 wt% of carbon. The addition of additives decreased the bloating activation temperature, and viscous behavior was promoted in the core portion of the aggregates, resulting in a difference in the melting point between the shell and the core. As a result, the occurrence of adhesion at the aggregates surface was suppressed.

The purpose of this study is to compare the bloating mechanism of artificial lightweight aggregate under sintering and rapid sintering conditions to identify the factors behind the bloating of the lightweight aggregate under these sintering conditions, and to find suitable temperature ramping conditions. The aggregate had an average particle size of 10 mm as formed using acid clay, and it was fired by a rapid sintering method and a normal sintering method. The bulk density and water absorption ratio of the specimen were measured, and the cross section was observed. No black core was observed under the rapid sintering condition, and it was lightened at an inflection point of 1150 °C. A reduction in the bulk density was observed in a shorter period of time when the input temperature was high under the normal sintering conditions. Regardless of the input temperature, the bulk density change was divided into three sections and a bloating-activation zone was observed in which the density abruptly decreased.

The purpose of this study was to improve the recycling rate of industrial wastes by investigating the bloating mechanism of artificial lightweight aggregate depending on the ramping rate and time, which is a dynamic parameter in the production of artificial lightweight aggregate. In this study, coal bottom ash and dredged soil at a weight ratio of 1 : 1 from a domestic power plant were used as raw materials. The artificial lightweight aggregates were formed by using an extruder and pelletizer (φ = 10 mm) and sintered by rapid sintering, 2-step firing, and normal sintering method. The physical properties of the aggregates such as bulk density, water absorption ratio, and microstructure of cross section are investigated with the sintering time and temperature. As the result of bloating and trapping mechanism, black core could be inhibited as the firing time increased at the temperature before surface formation. As a result of firing schedule graphs using least square method, it was possible to manufacture artificial lightweight aggregate with micropores, specific gravity of 1.1, and absorption rate of 3% at a heating rate of 27°c/min or less.